高流动性高玻纤增强PA6 德国朗盛 DPBKC60EF 000000
PA6 德国朗盛 DPBKV60EF 000000
Lanxess Durethan DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber
产品说明：PA6,60%玻璃纤维填充,注射成型,改善流动性。
机械性能：
Tensile Strength at Break 158 MPa 22900 psi cond.; ISO 527-1, -2; 5 mm/min
230 MPa 33400 psi d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 2.5 % 2.5 % d.a.m.; ISO 527-1, -2; 5 mm/min
3.5 % 3.5 % cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 12.5 GPa 1810 ksi cond.; ISO 527-1, -2; 1 mm/min
20.0 GPa 2900 ksi d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 390 MPa
@Strain 3.00 % 56600 psi
@Strain 3.00 % d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 20.2 GPa 2930 ksi d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 18.0 kJ/m²
@Temperature 23.0 °C 8.57 ft-lb/in²
@Temperature 73.4 °F d.a.m.; ISO 180-1A
18.0 kJ/m²
@Temperature -30.0 °C 8.57 ft-lb/in²
@Temperature -22.0 °F cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²
@Temperature 23.0 °C 42.8 ft-lb/in²
@Temperature 73.4 °F d.a.m.; ISO 180-1U
90.0 kJ/m²
@Temperature 23.0 °C 42.8 ft-lb/in²
@Temperature 73.4 °F cond.; ISO 180-1U
90.0 kJ/m²
@Temperature -30.0 °C 42.8 ft-lb/in²
@Temperature -22.0 °F d.a.m.; ISO 180-1U
90.0 kJ/m²
@Temperature -30.0 °C 42.8 ft-lb/in²
@Temperature -22.0 °F cond.; ISO 180-1U
Charpy Impact Unnotched 9.50 J/cm²
@Temperature 23.0 °C 45.2 ft-lb/in²
@Temperature 73.4 °F d.a.m.; ISO 179-1eU
9.50 J/cm²
@Temperature -30.0 °C 45.2 ft-lb/in²
@Temperature -22.0 °F d.a.m.; ISO 179-1eU
Charpy Impact, Notched 1.70 J/cm²
@Temperature 23.0 °C 8.09 ft-lb/in²
@Temperature 73.4 °F d.a.m.; ISO 179-1eA
1.70 J/cm²
@Temperature -30.0 °C 8.09 ft-lb/in²
@Temperature -22.0 °F d.a.m.; ISO 179-1eA
Puncture Energy 3.70 J
@Load