二硫化钼润滑高温尼龙66 美国LNP RFN18SXS
PA66 美国液氮 RFN18SXS
玻璃纤维增强材料 添加二硫化钼润滑剂 热稳定剂 ROHS合规 (RFL-4218 HS)
SABIC Innovative Plastics LNP LUBRICOMP RFN18SXS PA 66
LNP* Lubricomp* RFN18SXS 尼龙66树脂含有玻璃纤维，二硫化钼化合物。这种材料的性能特点：热稳定。
物性数据：
Physical Properties Metric English Comments
Density 1.51 g/cc 0.0546 lb/in³ ISO 1183
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm 0.0015 - 0.0035 in/in on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 219 MPa 31800 psi 5 mm/min; ISO 527
Elongation at Break 2.8 % 2.8 % 5 mm/min; ISO 527
Tensile Modulus 13.3 GPa 1930 ksi 1 mm/min; ISO 527
Flexural Strength 311 MPa 45100 psi break, 2 mm/min; ISO 178
Flexural Modulus 11.1 GPa 1610 ksi 2 mm/min; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m² 5.71 ft-lb/in² 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 75.0 kJ/m² 35.7 ft-lb/in² 80*10*4; ISO 180/1U
Coefficient of Friction, Dynamic 0.75 0.75 ASTM D3702 Modified
Coefficient of Friction, Static 0.59 0.59 ASTM D3702 Modified
K (wear) Factor 90.6 x 10-8 mm³/N-M 45.0 x 10-10 in³-min/ft-lb-hr Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 261 °C 502 °F Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 254 °C 489 °F Flatw 80*10*4 sp=64mm; ISO 75/Af