无卤阻燃尼龙66/6 Starflam R10002E
PA66 基础创新塑料(美国) R10002E-BK1B568
无卤无磷阻燃 ROHS合规 (R1000Z220EM)
Eurostar Starflam R10002E PA66/6, Injection Molded
Starflam R10002E是一个非填充，无卤素和无红磷的阻燃的聚酰胺66/聚酰胺6注塑树脂（又称R1000Z220EM ）
机械性能：
Tensile Strength at Break 75.0 MPa 10900 psi ISO 527
Elongation at Break 5.00 % 5.00 % ISO 527
Tensile Modulus 3.40 GPa 493 ksi 1 mm/min; ISO 527
Flexural Strength 105 MPa 15200 psi ISO 178
Flexural Modulus 3.50 GPa 508 ksi ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m² 1.90 ft-lb/in² 80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m² 28.6 ft-lb/in² 80x10x4; ISO 180/1U
热性能：
Deflection Temperature at 0.46 MPa (66 psi) 200 °C 392 °F Flatw 80x10x4, sp=64 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C 176 °F Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 65.0 °C
@Thickness 0.400 mm 149 °F
@Thickness 0.0157 in
120 °C
@Thickness 0.800 mm 248 °F
@Thickness 0.0315 in
120 °C
@Thickness 1.60 mm 248 °F
@Thickness 0.0630 in
120 °C
@Thickness 3.00 mm 248 °F
@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C
@Thickness 0.400 mm 149 °F
@Thickness 0.0157 in
65.0 °C
@Thickness 0.800 mm 149 °F
@Thickness 0.0315 in
75.0 °C
@Thickness 1.60 mm 167 °F
@Thickness 0.0630 in
75.0 °C
@Thickness 3.00 mm 167 °F
@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C
@Thickness 0.400 mm 149 °F
@Thickness 0.0157 in
85.0 °C
@Thickness 0.800 mm 185 °F
@Thickness 0.0315 in
85.0 °C
@Thickness 1.60 mm 185 °F
@Thickness 0.0630 in
85.0 °C
@Thickness 3.00 mm 185 °F
@Thickness 0.118 in
Flammability, UL94 V-0
@Thickness 0.400 mm V-0
@Thickness 0.0157 in IEC
V-0
@Thickness 0.800 mm V-0
@Thickness 0.0315 in IEC
V-0
@Thickness 1.60 mm V-0
@Thickness 0.0630 in IEC
V-0
@Thickness 3.00 mm V-0
@Thickness 0.118 in IEC