POM美国杜邦 500P NC010热稳定级 耐老化耐候

聚甲醛为白色粉末，一般不透明，着色性好，比重1.41-1.43克/立方厘米，成型收缩率1.2-3.0%，成型温度170-200℃，干燥条件80-90℃2小时。POM的长期耐热性能不高，但短期可达到160℃，其中均聚POM短期耐热比共聚POM高10℃以上，但长期耐热共聚POM反而比均聚POM高10℃左右。可在-40℃~100℃温度范围内长期使用。POM极易分解，分解温度为280℃，分解时有刺激性和腐蚀性气体发生。故模具钢材宜选用耐腐蚀性的材料制作。

Polyformaldehyde is a white powder, generally opaque, with good coloring properties. Its specific gravity is 1.41-1.43 grams per cubic centimeter, and its molding shrinkage is 1.2-3.0%. The molding temperature is 170-200 ℃, and the drying condition is 80-90 ℃ for 2 hours. The long-term heat resistance of POM is not high, but it can reach 160 ℃ in the short term. Among them, the short-term heat resistance of homopolymer POM is more than 10 ℃ higher than that of copolymer POM, but the long-term heat resistance of copolymer POM is actually about 10 ℃ higher than that of homopolymer POM. It can be used for a long time within the temperature range of -40 ℃ to 100 ℃. POM is highly prone to decomposition, with a decomposition temperature of 280 ℃. During decomposition, irritating and corrosive gases may occur. Therefore, the mold steel should be made of corrosion-resistant materials. Полиформальдегид для белого порошка, как правило, непрозрачный, хорошая окраска, удельный вес 1,41 - 1,43 г / см3, скорость усадки формования 1,2 - 3,0%, температура формования °C, условия сушки 80 - 90 °C 2 часа.  Долгосрочная теплостойкость POM невелика, но в краткосрочной перспективе может достигать 160 ° C, из которых краткосрочная теплостойкость POM выше, чем у POM, но долгосрочная теплостойкость POM выше, чем у POM примерно на 10 ° C.  Может использоваться в течение длительного времени при температуре от - 40°C до 100°C.  POM очень легко разлагается, температура разложения составляет 280°C, при разложении происходит раздражающий и коррозионный газ.  Поэтому пресс - форма сталь должна быть изготовлена из коррозионно - стойких материалов.