POM韩国可隆K300LO物性表物理性能测试条件测试方法测试结果单位收缩率MDISO294-42.2%吸水率23°C,24hrISO620.58%平衡,23°C,60%RHASTMD5700.22%熔体质量流动速率190°C/2.16kgASTMD12389.0g/10min190°C/2.16kgISO11339.0g/10min收缩率MDASTMD9552.0%TDISO294-42.2%机械性能测试条件测试方法测试结果单位弯曲应力23°CISO17883.0Mpa抗张强度23°CASTMD63862.0Mpa拉伸应力屈服,23°CISO527-264.0Mpa伸长率断裂,23°CASTMD63865%拉伸应变断裂,23°CISO527-230%弯曲模量23°CASTMD7902300Mpa23°CISO1782650Mpa弯曲强度23°CASTMD79090.0Mpa热性能测试条件测试方法测试结果单位热变形温度0.45MPa,未退火ASTMD648158°C1.8MPa,未退火ASTMD648110°C1.8MPa,未退火ISO75-2/A95.0°C维卡软化温度ASTMD1525162°C熔融温度ISO°CASTMD1525166°C线形热膨胀系数MDASTMD6961.3E-04cm/cm/°C电气性能测试条件测试方法测试结果单位表面电阻率ASTMD2571E+13ohmsIEC600931E+16ohms体积电阻率ASTMD2571E+11ohms·cmIEC600931E+14ohms·cm介电强度ASTMD14919KV/mmIECKV/mm介电常数ASTMD1503.70耗散因数1MHzASTMD1506E-03②冷却回化时放出热量大，要充分冷却。③熔融态与固态的比重差大，成型收缩大，易发生缩孔、气孔。④冷却快，结晶度低，收缩小，透明度高。结晶度与塑件壁厚有关，壁厚则冷却慢，结晶度高，收缩大，物性好。所以结晶性料应按要求必须控制模温。