Polyamide 12
LATI S.p.A.
碳纳米填料
产品说明：
Partially conductive/dissipative compound based on Polyamide 12 (PA 12).
Carbon nanotubes.
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 收缩率 1 | ISO 294-4 | ||
| 垂直流动方向 : 2.00 mm | 1.8 到 2.2 | % | ISO 294-4 |
| 流动方向 : 2.00 mm | 1.6 到 2.0 | % | ISO 294-4 |
| 拉伸模量 (23°C) | 1900 | MPa | ISO 527-2/1 |
| 拉伸应力 (断裂, 23°C) | 50.0 | MPa | ISO 527-2/5 |
| 拉伸应变 (断裂, 23°C) | 7.0 | % | ISO 527-2/5 |
| 简支梁缺口冲击强度 (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 (23°C) | 60 | kJ/m² | ISO 179/1eU |
| 悬壁梁缺口冲击强度 (23°C) | 80 | J/m | ASTM D256A |
| 热变形温度 | |||
| 0.45 MPa, 未退火 | 120 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 55.0 | °C | ISO 75-2/A |
| 维卡软化温度 | 150 | °C | ISO 306/B50 |
| 表面电阻率 | 10 | ohms | ASTM D257 |
| 干燥温度 | 70.0 到 90.0 | °C | |
| 干燥时间 | 3.0 | hr | |
| 加工（熔体）温度 | 190 到 220 | °C | |
| 模具温度 | 70.0 到 90.0 | °C | |
| 注射速度 | 中等 |
| 1 . | at 60 MPa of cavity pressure |
产品 供货地区 产品说明
Latiohm 57D-05 PD01 G/15 Partially conductive/dissipative compound based on...
Latiohm 62-03 PD01 G/20 Partially conductive/dissipative compound based on...
Latiohm 62-08 PD02 G/30 Dissipative compound based on Polyamide 6 (PA 6). ...
Latiohm 62-09 PD01 G/20-V2HF Dissipative compound based on Polyamide 6 (PA 6). ...
Latiohm 63-08 PD02 G/25 Dissipative compound based on Polyamide 6 (PA 6), ...
Latiohm 66-04 PD01 G/25-V0CT1 Partially conductive/dissipative compound based on...
Latiohm 66-05 PD01 G/20 Partially conductive/dissipative compound based on...
Latiohm 66-06 PD03 G/20 Partially conductive/dissipative compound based on...
Latiohm 66-07 PD08 G/30 Semiconductive/dissipative product based on Polyam...
Latiohm 66-08 PD02 G/35 Dissipative compound based on Polyamide 66 (PA 66)...
Latiohm 66-10 H2 CNT CE/10 Dissipative compound based on Polyamide 66 (PA 66)...
Latiohm 66-10 H2 CNT G/35 Partially conductive/dissipative compound based on...
Latiohm 82-01 CNT Partially conductive/dissipative compound based on...