美国杜邦70G33HR-L增韧级耐低温尼龙玻纤增强PA66产品描述颜色特性玻纤增强应用领域电气应用;体育用品物性表机械性能测试条件测试方法测试结果单位埃佐冲击强度ASTM D-256107J/m挠曲模量23℃,50%RHASTM D-7906205Mpa23℃,DAMASTM D-7908963Mpa挤剪强度23℃,DAMASTM D-73286Mpa断裂伸长率23℃,50%RHASTM D-6384%泰伯磨耗量50%RH14cycles拉伸强度23℃,50%RHASTM D-638124.1Mpa挠曲强度23℃,DAMASTM D-790262Mpa洛氏硬度MDAMASTM D-785M101断裂伸长率23℃,DAMASTM D-6383%拉伸强度23℃,DAMASTM D-638196.1Mpa埃佐冲击强度23℃,50%RHASTM D-256133J/m热性能测试条件测试方法测试结果单位熔点50%RHASTM D-789255°CDAMASTM D-789255°C线性热膨胀系数ASTM D-6962.3×10m/m/℃热畸变温度1.8MPaASTM D-648249°C电气性能测试条件测试方法测试结果单位损耗因数DAM@10ASTM D-1500.02介电强度DAMASTM D-149530volts/mil介电常数DAM@10ASTM D-1503.7介电强度分步法(DAM)ASTM D-149440volts/mil体积电阻率DAMASTM D-25710ohm-cm****RHASTM D-25710ohm-cm介电常数DAM@10ASTM D-RH@10ASTM D-RH@10ASTM D-15025.0基本性能测试条件测试方法测试结果单位吸水率24小时浸渍(23℃)ASTM D-5700.7%饱和(23℃)ASTM D-5705.4%