POM 韩国可隆 UR304物性表物理性能测试条件测试方法测试结果单位密度 / 比重ASTMD792,ISO11831.36g/cm³熔体质量流动速率190°C/2.16kgASTMD123812g/10min190°C/2.16kgISO11337.5g/10min收缩率MDASTMD9551.7%TDISO294-42.2%MDISO294-42.0%吸水率23°C,24hrISO620.63%平衡,23°C,60%RHASTMD5700.25%机械性能测试条件测试方法测试结果单位抗张强度屈服,23°CASTMD63845.0Mpa23°CISO527-245.0Mpa伸长率屈服,23°CASTMD638140%断裂,23°CISO527-2>50%弯曲模量23°CASTMD7901800Mpa23°CISO1781900Mpa弯曲强度23°CASTMD79060.0Mpa23°CISO17855.0Mpa热性能测试条件测试方法测试结果单位热变形温度0.45MPa,未退火ASTMD648145°C1.8MPa,未退火ASTMD64882.0°C1.8MPa,未退火ISO75-2/A72.0°C熔融温度ISO°C线形热膨胀系数MDASTMD6961.3E-04cm/cm/°C均聚物和共聚物都是填充填料(玻璃纤维、含氟聚合物、芳族聚酰胺纤维和其他填料)制成增韧级、紫外线光稳定级材料。缩醛树脂与聚氨酯弹性体共混提高其韧性，