POM 韩国可隆 K500HS物理性能测试条件测试方法测试结果单位熔体质量流动速率190°C/2.16kgASTMD123814g/10min190°C/2.16kgISO113315g/10min收缩率MDASTMD9552.0%TDISO294-42.2%MDISO294-42.3%吸水率23°C,24hrISO620.53%平衡,23°C,60%RHASTMD5700.22%机械性能测试条件测试方法测试结果单位抗张强度23°CASTMD63866.0Mpa拉伸应力屈服,23°CISO527-267.0Mpa伸长率断裂,23°CASTMD63855%拉伸应变断裂,23°CISO527-230%弯曲模量23°CASTMD7902900Mpa23°CISO1782950Mpa弯曲强度23°CASTMD79098.0Mpa弯曲应力23°CISO17895.0Mpa热性能测试条件测试方法测试结果单位热变形温度0.45MPa,未退火ASTMD648A158°C1.8MPa,未退火ASTMD648A110°C1.8MPa,未退火ISO75-2/A100°C维卡软化温度ASTMD1525162°C熔融温度ISO°CASTMD1525173°C线形热膨胀系数MDASTMD6961.3E-05cm/cm/°CPOM医疗器材 可作医疗用途的杯、筒、瓶以及牙科器械、药品容器和手术器械，甚至还可用作人工肾、人工肺等人工脏器