PA66巴斯夫A3GE6耐磨损高流动增强级材料 产品描述颜色特性高流动;耐油应用领域电气应用;工业机械物性表物性性能测试条件测试方法测试结果单位密度ASTM D792/ISO 11831360成型收缩率ASTM D9550.55%熔融指数（流动系数）ASTM D1238/ISO 113340 （cm3/10min 275℃/5kg )g/10min吸水率 23℃/24HASTM D570/ISO 621.5-1.9%机械性能测试条件测试方法测试结果单位拉伸模量ASTM D638/ISO 52710000kg/cm²(MPa)[Lb/in²]弯曲模量ASTM D790/ISO 1788600kg·cm/cm(J/M)ft·lb/in弯曲强度ASTM D790/ISO 178280kg·cm/cm(J/M)ft·lb/inCharpy冲击强度ASTM D256/ISO 17985kg·cm/cm(J/M)ft·lb/inASTM D256/ISO 17913kg·cm/cm(J/M)ft·lb/inASTM D256/ISO 17911kg·cm/cm(J/M)ft·lb/inASTM D256/ISO 17970kg·cm/cm(J/M)ft·lb/inIZOD 缺口冲击强度ASTM D256/ISO 17911.5kg·cm/cm(J/M)ft·lb/in拉伸断裂伸长率(延伸率)ASTM D638/ISO 5273%热性能测试条件测试方法测试结果单位热变形温度ASTM D648/ISO 75240(1.80MPa)℃（℉）熔点260℃（℉）线性膨胀系数ASTM D696/ISO mm/mm.℃电气性能测试条件测试方法测试结果单位介电常数ASTM D150/IEC 602503.5体积电阻率ASTM D257/IEC 600931E 13Ω.cm