高刚性PA66 德国巴斯夫 A3WG6 加纤30% 绝缘材料 容器 机械部件Ultramid® A3WG6Polyamide 66BASF Corporation30% 玻璃纤维增强材料产品说明：Ultramid A3WG6 is a 30% glass fiber reinforced and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.ApplicationsTypical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.物性信息：基本信息黄卡编号E36632-531632E41871-233745E41871-101468834填料/增强材料玻璃纤维增强材料, 30% 填料按重量特性尺寸稳定性良好刚性，高耐热性，中等耐油性能用途机器/机械部件绝缘材料汽车领域的应用容器外壳机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规形式粒子加工方法注射成型多点数据Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)物理性能干燥调节后的单位制测试方法比重1.36--g/cm³ASTM D792, ISO 1183溶化体积流率（MVR） (275°C/5.0 kg)40.0--cm³/10minISO 1133收缩率 - 流动 (3.18 mm)0.30--%吸水率 饱和5.5--%ASTM D570 饱和, 23°C5.5--%ISO 62 平衡, 50% RH1.7--%ASTM D570 平衡, 23°C, 50% RH1.7--%ISO 62机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)100007200MPaISO 527-2抗张强度 断裂, 23°C186--MPaASTM D638 断裂, 23°C190130MPaISO 527-2 断裂, 121°C93.074.0MPaISO 527-2伸长率 断裂, 23°C3.0--%ASTM D638 断裂, 23°C3.05.0%ISO 527-2弯曲模量 23°C8480--MPaASTM D790 23°C8600--MPaISO 178冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度ISO 179 -30°C11--kJ/m²ISO 179 23°C1322kJ/m²ISO 179简支梁无缺口冲击强度ISO 179 -30°C70--kJ/m²ISO 179 23°C85100kJ/m²ISO 179悬壁梁缺口冲击强度 -40°C91--J/mASTM D256 23°C110--J/mASTM D256 23°C12--kJ/m²ISO 180热性能干燥调节后的单位制测试方法载荷下热变形温度 0.45 MPa, 未退火250--°CASTM D648, ISO 75-2/B 1.8 MPa, 未退火250--°CASTM D648, ISO 75-2/A熔融峰值温度260--°CASTM D3418, ISO 3146高刚性PA66 德国巴斯夫 A3WG6 加纤30% 绝缘材料 容器 机械部件