增强级 PA66 德国巴斯夫 A3WG6-BK 尺寸稳定 耐热 型材 汽车领域应用 Ultramid® A3WG6 BK00564Polyamide 66BASF Corporation30% 玻璃纤维增强材料产品说明：Ultramid A3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. A3EG6 is the preferred grade for producing electrically insulating parts.ApplicationsTypical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.物性信息：基本信息黄卡编号E36632-531632E41871-233745E41871-101468834填料/增强材料玻璃纤维增强材料, 30% 填料按重量特性尺寸稳定性良好刚性，高耐热性，中等耐油性能用途机器/机械部件汽车领域的应用容器外壳型材机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规外观黑色形式粒子加工方法注射成型物理性能额定值单位制测试方法密度1.36g/cm³ISO 1183吸水率ISO 62 饱和, 23°C5.5%ISO 62 平衡, 23°C, 50% RH1.7%ISO 62机械性能额定值单位制测试方法拉伸应力 (断裂, 23°C)179MPaISO 527-2拉伸应变 (断裂, 23°C)2.6%ISO 527-2弯曲模量 (23°C)8730MPaISO 178冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°C)8.5kJ/m²ISO 180热性能额定值单位制测试方法热变形温度 (1.8 MPa, 未退火)250°CISO 75-2/A溶融温度（DSC）260°CISO 3146RTI ElecUL 746 0.710 mm125°CUL 746 1.50 mm125°CUL 746 3.00 mm125°CUL 746RTI ImpUL 746 1.50 mm115°CUL 746 3.00 mm120°CUL 746RTIUL 746 1.50 mm115°CUL 746 3.00 mm130°CUL 746可燃性额定值测试方法UL 阻燃等级UL 94 0.710 mmHBUL 94 1.50 mmHBUL 94 3.00 mmHBUL 94注射额定值单位制干燥温度80.0°C干燥时间2.0 到 4.0hr建议的最大水分含量0.15%加工（熔体）温度280 到 305°C模具温度80.0 到 90.0°C注塑压力3.50 到 12.5MPa注射速度快速增强级 PA66 德国巴斯夫 A3WG6-BK 尺寸稳定 耐热 型材 汽车领域应用 德国巴斯夫pa66,A3WG6-BK ,增强级 PA66, 耐热级PA66,pa66塑胶原料