Ultramid® 德国巴斯夫 PA66 A3X2G5 加纤25% 耐油性 阻燃 电气性能Ultramid® A3X2G5Polyamide 66BASF Corporation25% 玻璃纤维增强材料产品说明：Ultramid A3X2G5 is a 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term performance. Flame retardant based on red phosphorus; outstanding mechanical and electrical properties.物性信息：基本信息黄卡编号E36632-531634E41871-100497758E41871-233750填料/增强材料玻璃纤维增强材料, 25% 填料按重量添加剂阻燃性特性良好的电气性能耐油性能阻燃性机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规形式粒子加工方法注射成型多点数据Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Viscosity vs. Shear Rate (ISO 11403-2)物理性能干燥调节后的单位制测试方法比重1.34--g/cm³ASTM D792, ISO 1183溶化体积流率（MVR） (275°C/5.0 kg)40.0--cm³/10minISO 1133收缩率 - 流动 (3.18 mm)0.50--%吸水率 饱和6.0--%ASTM D570 饱和, 23°C6.0--%ISO 62 平衡, 50% RH1.4--%ASTM D570 平衡, 23°C, 50% RH1.4--%ISO 62机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)85006000MPaISO 527-2抗张强度 断裂, 23°C138--MPaASTM D638 断裂, -40°C196--MPaISO 527-2 断裂, 23°C140100MPaISO 527-2伸长率 断裂, 23°C3.0--%ASTM D638 断裂, 23°C3.04.5%ISO 527-2弯曲模量 (23°C)7100--MPaASTM D790冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度ISO 179 -30°C10--kJ/m²ISO 179 23°C1317kJ/m²ISO 179简支梁无缺口冲击强度ISO 179 -30°C6065kJ/m²ISO 179 23°C6570kJ/m²ISO 179悬壁梁缺口冲击强度ASTM D256 -40°C64--J/mASTM D256 23°C75--J/mASTM D256热性能干燥调节后的单位制测试方法载荷下热变形温度 0.45 MPa, 未退火250--°CASTM D648, ISO 75-2/B 1.8 MPa, 未退火238--°CASTM D648 1.8 MPa, 未退火250--°CISO 75-2/A熔融峰值温度260--°CASTM D3418, ISO 3146Ultramid® 德国巴斯夫 PA66 A3X2G5 加纤25% 耐油性 阻燃 电气性能德国巴斯夫 PA66 ,A3X2G5 ,耐油性pa66,阻燃PA66,增强级PA66