Novaduran的机械性能、刚性、抗热老化及抗药性都非常优越。 成型性能、抗磨损性、着色性能、电力特性都有极好的表现。 近来，PBT的需求增长迅速，特别是在电子和汽车工业。 三菱工程塑料株式会社在PBT的生产中采用对邻苯二甲酸二甲酯和1, 4-丁二醇为原材料，并使用一套完善的制造流程。

特点：

机械性能优越

耐热性能优越

成型性能和流动性佳

高尺寸稳定性、低湿气吸收率

表面色泽表现佳

耐油、耐药性卓越

电性能优越

耐摩擦和耐磨损性能优越

还具备阻燃性

5010CR218 (250°C/2.16 kg)1.312540 (2.0 mm/min)4.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010R3 218 (250°C/2.16 kg)1.312300 (2.0 mm/min)6.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010R521 (250°C/2.16 kg)1.312300 (2.0 mm/min)6.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010R5 L26 (250°C/2.16 kg)1.312300 (2.0 mm/min)6.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010R5 L235 (250°C/2.16 kg)1.312350 (2.0 mm/min)4.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010R7U3X31 (250°C/5.0 kg)1.42720 (2.0 mm/min)4.0 (23°C)

5010R8 L27 (250°C/2.16 kg)1.32000 (2.0 mm/min)5.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010R8 M31 (250°C/2.16 kg)1.31650 (2.0 mm/min)6.0 (23°C)HB (0.8 mm); HB (1.6 mm); HB (3.2 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)PLC 0

5010TR X514 (250°C/2.16 kg)1.262200 (2.0 mm/min)10 (23°C)HB (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5010TR XA19 (250°C/2.16 kg)1.272250 (2.0 mm/min)7.0 (23°C)HB (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

502010 (250°C/2.16 kg)1.312300 (2.0 mm/min)5.0 (23°C)

50268.00 (250°C/2.16 kg)1.312300 (2.0 mm/min)5.0 (23°C)

5505S25 (250°C/2.16 kg)1.28740 (2.0 mm/min)13 (23°C)HB (1.5 mm)

5510S33 (250°C/2.16 kg)1.24360 (2.0 mm/min)30 (23°C)HB (1.5 mm)75.0 (1.5 mm)75.0 (1.5 mm)75.0 (1.5 mm)

5010N120 (250°C/2.16 kg)2780 (2.0 mm/min)2.0 (23°C)1.43V-0 (0.71 mm); V-0 (1.5 mm); V-0 (3.0 mm)PLC 3150 (0.71 mm)130 (0.71 mm)130 (0.71 mm)

5010N521 (250°C/2.16 kg)2500 (2.0 mm/min)3.0 (23°C)1.42V-2 (0.8 mm)75.0 (0.8 mm)75.0 (0.8 mm)75.0 (0.8 mm)

5010N6 220 (250°C/2.16 kg)2600 (2.0 mm/min)3.0 (23°C)1.43V-0 (0.71 mm); V-0 (1.6 mm); V-0 (3.2 mm)PLC 1140 (0.71 mm)120 (0.71 mm)140 (0.71 mm)

5010N6 3X20 (250°C/2.16 kg)2500 (2.0 mm/min)3.0 (23°C)1.43V-0 (0.71 mm); V-0 (1.5 mm); V-0 (3.0 mm)PLC 1140 (0.71 mm)120 (0.71 mm)140 (0.71 mm)

5010N6-620 (250°C/2.16 kg)2600 (2.0 mm/min)3.0 (23°C)1.43V-0 (0.30 mm); V-0 (0.71 mm); V-0 (1.6 mm); V-0 (3.2 mm)PLC 175.0 (0.30 mm); 140 (0.71 mm)75.0 (0.30 mm); 140 (0.71 mm)75.0 (0.30 mm); 140 (0.71 mm)

5010N6-8S387 (250°C/2.16 kg)590 (2.0 mm/min)5.6 (23°C)V-2 (0.75 mm); V-0 (0.75 mm)PLC 2

5710N1TX12 (250°C/5.0 kg)2400 (2.0 mm/min)54 (23°C)1.32V-0 (1.5 mm); V-0 (3.0 mm); 5VA (3.0 mm)PLC 075.0 (1.5 mm)75.0 (1.5 mm)75.0 (1.5 mm)

5710N1X8.00 (250°C/2.16 kg)2400 (2.0 mm/min)6.0 (23°C)1.4V-0 (0.75 mm); V-0 (1.5 mm); V-0 (3.0 mm)PLC 375.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5710N27.00 (250°C/2.16 kg)2350 (2.0 mm/min)5.0 (23°C)1.36V-0 (0.75 mm); V-0 (1.5 mm); V-0 (3.0 mm)PLC 275.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5810N2 115 (250°C/2.16 kg)2600 (2.0 mm/min)3.0 (23°C)1.34

SEF-500T5.00 (250°C/2.16 kg)2200 (2.0 mm/min)6.0 (23°C)1.31V-0 (0.75 mm); V-0 (1.6 mm); V-0 (3.2 mm)PLC 075.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5010F6 X425 (250°C/5.0 kg)1.626600 (2.0 mm/min)5.0 (23°C)40 (Unspecified)HB (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5010G1565 (250°C/5.0 kg)1.415500 (2.0 mm/min)7.0 (23°C)15 (Glass Fiber)HB (0.8 mm); HB (1.5 mm); HB (3.0 mm); HB (6.0 mm)130 (0.8 mm)75.0 (0.8 mm)140 (0.8 mm)

5010G15EF90 (250°C/5.0 kg)1.415300 (2.0 mm/min)7.0 (23°C)15 (Glass Fiber)

5010G3040 (250°C/5.0 kg)1.539000 (2.0 mm/min)10 (23°C)30 (Glass Fiber)HB (0.8 mm); HB (1.5 mm); HB (3.0 mm); HB (6.0 mm)140 (0.8 mm)120 (0.8 mm)140 (0.8 mm)PLC 1

5010G30 X430 (250°C/5.0 kg)1.539100 (2.0 mm/min)11 (23°C)30 (Glass Fiber)HB (0.8 mm); HB (1.5 mm); HB (3.0 mm); HB (6.0 mm)140 (0.8 mm)120 (0.8 mm)140 (0.8 mm)PLC 1

5010G30EF55 (250°C/5.0 kg)1.58600 (2.0 mm/min)12 (23°C)30 (Glass Fiber)

5010G30TZ8.00 (250°C/5.0 kg)1.58000 (2.0 mm/min)12 (23°C)30 (Glass Fiber)HB (0.8 mm); HB (1.5 mm); HB (3.0 mm); HB (6.0 mm)PLC 1

5010G4515 (250°C/5.0 kg)1.6714500 (2.0 mm/min)14 (23°C)45 (Glass Fiber)HB (0.75 mm); HB (1.5 mm); HB (3.0 mm)75.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)PLC 1

5010GP2023 (250°C/5.0 kg)1.498900 (2.0 mm/min)8.0 (23°C)40 (Unspecified)

5010GT1550 (250°C/5.0 kg)1.45000 (2.0 mm/min)6.0 (23°C)15 (Glass Fiber)HB (1.5 mm)

5010GT15 X14 (250°C/5.0 kg)1.394000 (2.0 mm/min)12 (23°C)15 (Glass Fiber)HB (1.5 mm)

5010GT3025 (250°C/5.0 kg)1.518600 (2.0 mm/min)10 (23°C)30 (Glass Fiber)

5010GW15-162 (250°C/5.0 kg)1.535300 (2.0 mm/min)3.0 (23°C)

5010GX30HS33 (250°C/5.0 kg)1.497500 (2.0 mm/min)18 (23°C)30 (Glass Fiber)

5308F2055 (265°C/2.16 kg)1.495000 (2.0 mm/min)2.0 (23°C)20 (Unspecified)

5308FDV50 (265°C/2.16 kg)1.333000 (2.0 mm/min)2.0 (23°C)

5308FDV-K2D48 (265°C/2.16 kg)1.332950 (2.0 mm/min)2.0 (23°C)

5308G30 HX339 (280°C/2.16 kg)1.529000 (2.0 mm/min)8.0 (23°C)30 (Glass Fiber)HB (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5308G30MG47 (265°C/5.0 kg)1.569700 (2.0 mm/min)8.0 (23°C)30 (Glass Fiber)

5308G559.00 (265°C/5.0 kg)1.8117900 (2.0 mm/min)10 (23°C)55 (Glass Fiber)

5010CTN338700 (2.0 mm/min)5.0 (23°C)16 (250°C/5.0 kg)1.7133 (Unspecified)V-0 (0.75 mm)PLC 175.0 (0.75 mm)75.0 (0.75 mm)75.0 (0.75 mm)

5010FN6UX2 LAW259Z10000 (2.0 mm/min)4.0 (23°C)12 (250°C/5.0 kg)1.7333 (Glass Milled\Glass Fiber)

5010GN1-15 AM6200 (2.0 mm/min)6.3 (23°C)40 (250°C/5.0 kg)1.5415 (Glass Fiber)V-0 (0.71 mm)PLC 3130 (0.71 mm)120 (0.71 mm)130 (0.71 mm)

5010GN1-15-8S5400 (2.0 mm/min)6.5 (23°C)65 (250°C/5.0 kg)1.5215 (Glass Fiber)V-0 (0.71 mm)PLC 3130 (0.71 mm)130 (0.71 mm)130 (0.71 mm)

5010GN1-20 AM7200 (2.0 mm/min)6.0 (23°C)40 (250°C/5.0 kg)1.5820 (Glass Fiber)V-0 (0.71 mm)PLC 3130 (0.71 mm)120 (0.71 mm)130 (0.71 mm)

5010GN1-30 AM210500 (2.0 mm/min)10 (23°C)30 (250°C/5.0 kg)1.6630 (Glass Fiber)V-0 (0.71 mm)PLC 3130 (0.71 mm)120 (0.71 mm)130 (0.71 mm)

5010GN1-30 X410500 (2.0 mm/min)8.3 (23°C)30 (250°C/5.0 kg)1.6530 (Glass Fiber)V-0 (0.71 mm)PLC 3130 (0.71 mm)120 (0.71 mm)130 (0.71 mm)

5010GN1-30NX18000 (2.0 mm/min)7.0 (23°C)35 (250°C/5.0 kg)1.6130 (Glass Fiber)V-0 (0.71 mm)PLC 3140 (0.75 mm)140 (0.75 mm)140 (0.75 mm)

5010GN1-30TX28930 (2.0 mm/min)11 (23°C)24 (250°C/5.0 kg)1.630 (Glass Fiber)PLC 3

5010GN2-156400 (2.0 mm/min)6.0 (23°C)48 (250°C/5.0 kg)1.5415 (Glass Fiber)V-0 (0.8 mm); V-0 (3.0 mm)PLC 3130 (0.8 mm)120 (0.8 mm)130 (0.8 mm)

5010GN2-30TS9400 (2.0 mm/min)11 (23°C)14 (250°C/5.0 kg)1.6430 (Glass Fiber)V-0 (0.75 mm)

5010GN2-30X210500 (2.0 mm/min)9.0 (23°C)45 (250°C/5.0 kg)1.6630 (Glass Fiber)V-0 (0.8 mm); V-0 (1.5 mm); V-0 (3.0 mm); 5VA (1.5 mm); 5VA (3.0 mm)PLC 3140 (0.8 mm)130 (0.8 mm)140 (0.8 mm)

5010GN4-35C BK212400 (2.0 mm/min)10 (23°C)35 (250°C/10.0 kg)1.7435 (Glass Fiber)

5010GN6-053800 (2.0 mm/min)4.0 (23°C)30 (250°C/5.0 kg)1.475.0 (Glass Fiber)V-0 (0.70 mm)PLC 3140 (0.75 mm)130 (0.75 mm)140 (0.75 mm)

5010GN6-155890 (2.0 mm/min)4.0 (23°C)62 (250°C/5.0 kg)1.5915 (Glass Fiber)V-0 (0.75 mm)PLC 2130 (0.75 mm)130 (0.75 mm)140 (0.75 mm)

5010GN6-15M8 AM6100 (2.0 mm/min)7.0 (23°C)62 (250°C/5.0 kg)1.5515 (Glass Fiber)V-0 (0.75 mm)PLC 2130 (0.75 mm)130 (0.75 mm)140 (0.75 mm)

5010GN6-15M8 LT6300 (2.0 mm/min)4.0 (23°C)38 (250°C/5.0 kg)1.6115 (Glass Fiber)V-0 (0.75 mm)PLC 2130 (0.75 mm)130 (0.75 mm)140 (0.75 mm)

5010GN6-15M8X6500 (2.0 mm/min)6.8 (23°C)26 (250°C/5.0 kg)1.5715 (Glass Fiber)V-0 (0.30 mm); V-0 (1.5 mm); 5VA (1.5 mm)PLC 2130 (0.30 mm)130 (0.30 mm)140 (0.30 mm)

5010GN6-15T5900 (2.0 mm/min)8.0 (23°C)46 (250°C/5.0 kg)1.5315 (Glass Fiber)V-0 (0.75 mm)PLC 2130 (0.75 mm)130 (0.75 mm)140 (0.75 mm)