BASF Ultrason S 3010 PSU 物性表物理性能额定值 (公制)额定值 (英制)测试方法密度1.24 g/cc0.0448 lb/in³ISO 1183吸水率0.80 %0.80 %ISO 62平衡吸湿0.30 %0.30 %23°C/50% R.H.; ISO 62粘度测试72 cm³/g72 cm³/gViscosity number线性成型收缩率,Flow0.0070 cm/cm0.0070 in/inISO 294线性成型收缩率，横向0.0074 cm/cm0.0074 in/inISO 294熔体流动速率40 g/10 min@Load 10.0 kg, Temperature 360 °C40 g/10 min@Load 22.0 lb, Temperature 680 °FISO 1133机械性能额定值 (公制)额定值 (英制)测试方法球压硬度135 MPa19600 psiISO 2039-1抗张强度(断裂)75.0 MPa10900 psi5mm/min; ISO 527-2抗张强度20.0 MPa@Strain 1.00 %, Temperature 160 °C2900 psi@Strain 1.00 %, Temperature 320 °FISO 52727.0 MPa@Strain 1.00 %, Temperature 23.0 °C3920 psi@Strain 1.00 %, Temperature 73.4 °FISO 52735.0 MPa@Strain 2.00 %, Temperature 160 °C5080 psi@Strain 2.00 %, Temperature 320 °FISO 52747.0 MPa@Strain 2.00 %, Temperature 23.0 °C6820 psi@Strain 2.00 %, Temperature 73.4 °FISO 52770.0 MPa@Strain 4.00 %, Temperature 23.0 °C10200 psi@Strain 4.00 %, Temperature 73.4 °FISO 527抗张强度(屈服)75.0 MPa10900 psi50mm/min; ISO 527-240.0 MPa@Temperature 140 °C5800 psi@Temperature 284 °F58.0 MPa@Temperature 100 °C8410 psi@Temperature 212 °F68.0 MPa@Temperature 60.0 °C9860 psi@Temperature 140 °F75.0 MPa@Temperature 20.0 °C10900 psi@Temperature 68.0 °F伸长率 (断裂)5.7 %5.7 %5mm/min; ISO 527-2屈服伸长率5.7 %5.7 %50mm/min; ISO 527-20.50 %@Time 3600 sec, Pressure 10.0 MPa0.50 %@Time 1.00 hour, Pressure 1450 psiISO 8990.55 %@Pressure 10.0 MPa, Time 360000 sec0.55 %@Pressure 1450 psi, Time 100 hourISO 8990.56 %@Pressure 10.0 MPa, Time 3.60e+7 sec0.56 %@Pressure 1450 psi, Time 10000 hourISO 8990.80 %@Time 3600 sec, Pressure 20.0 MPa0.80 %@Time 1.00 hour, Pressure 2900 psiISO 8990.90 %@Pressure 20.0 MPa, Time 360000 sec0.90 %@Pressure 2900 psi, Time 100 hourISO 8991.3 %@Time 3600 sec, Pressure 30.0 MPa1.3 %@Time 1.00 hour, Pressure 4350 psiISO 8991.4 %@Pressure 30.0 MPa, Time 360000 sec1.4 %@Pressure 4350 psi, Time 100 hourISO 8991.5 %@Pressure 30.0 MPa, Time 3.60e+7 sec1.5 %@Pressure 4350 psi, Time 10000 hourISO 8991.9 %@Time 3600 sec, Pressure 40.0 MPa1.9 %@Time 1.00 hour, Pressure 5800 psiISO 8992.0 %@Pressure 20.0 MPa, Time 3.60e+7 sec2.0 %@Pressure 2900 psi, Time 10000 hourISO 8992.0 %@Pressure 40.0 MPa, Time 360000 sec2.0 %@Pressure 5800 psi, Time 100 hourISO 8992.0 %@Time 3600 sec, Pressure 42.0 MPa2.0 %@Time 1.00 hour, Pressure 6090 psiISO 8992.2 %@Pressure 42.0 MPa, Time 360000 sec2.2 %@Pressure 6090 psi, Time 100 hourISO 8992.4 %@Pressure 40.0 MPa, Time 3.60e+7 sec2.4 %@Pressure 5800 psi, Time 10000 hourISO 8992.5 %@Pressure 42.0 MPa, Time 3.60e+7 sec2.5 %@Pressure 6090 psi, Time 10000 hourISO 899Creep Strength17.0 MPa@Time 3.60e+7 sec2470 psi@Time 10000 hourin water at 95°C20.0 MPa@Time 3.60e+6 sec2900 psi@Time 1000 hourin water at 95°C25.0 MPa@Time 360000 sec3630 psi@Time 100 hourin water at 95°C32.0 MPa@Time 36000 sec4640 psi@Time 10.0 hourin water at 95°C弹性模量2.00 GPa@Temperature 140 °C290 ksi@Temperature 284 °FISO 5272.30 GPa@Temperature 100 °C334 ksi@Temperature 212 °FISO 5272.49 GPa@Temperature 60.0 °C361 ksi@Temperature 140 °FISO 5272.51 GPa@Temperature 20.0 °C364 ksi@Temperature 68.0 °FISO 527拉伸模量2.60 GPa377 ksiISO 527-2Fatigue Strength25.0 MPa@# of Cycles 1.00e+73630 psi@# of Cycles 1.00e+730.0 MPa@# of Cycles 1.00e+64350 psi@# of Cycles 1.00e+640.0 MPa@# of Cycles 1000005800 psi@# of Cycles 10000050.0 MPa@# of Cycles 100007250 psi@# of Cycles 10000剪切模量0.0250 GPa@Temperature 200 °C3.63 ksi@Temperature 392 °FISO 67210.800 GPa@Temperature 175 °C116 ksi@Temperature 347 °FISO 67210.900 GPa@Temperature 100 °C131 ksi@Temperature 212 °FISO 67210.950 GPa@Temperature 50.0 °C138 ksi@Temperature 122 °FISO 6721悬壁梁缺口冲击强度5.50 kJ/m²2.62 ft-lb/in²ISO 180/A5.00 kJ/m²@Temperature 120 °C2.38 ft-lb/in²@Temperature 248 °FISO 179/1eA6.00 kJ/m²@Temperature -30.0 °C2.86 ft-lb/in²@Temperature -22.0 °FISO 180/A10.0 kJ/m²@Temperature 50.0 °C4.76 ft-lb/in²@Temperature 122 °FISO 179/1eA13.0 kJ/m²@Temperature -25.0 °C6.19 ft-lb/in²@Temperature -13.0 °FISO 179/1eA