VALOX™ 310SE0 - SABIC PBT

VALOX™ FR Resin 310SE0 - Asia

Generic Name: Polybutylene Terephthalate (PBT) - Supplied by: SABIC

VALOX 310SE0 is an unreinforced, flame retardant Polybutylene Terephthalate (PBT) injection moldable grade with excellent chemical resistance. It has a UL94V0@0.71mm and 5VA@3.0mm flame rating. This is a good candidate for thin wall applications in the electrical industry including bobbins, keyboards, switches and appliance housings.

Compare to Typical Values - Upgrade to compare! Compare To Yellow Card(s)

Units: SI 

GENERAL
Material Status

Commercial: Active

UL Yellow Card 1

E207780-636460

Search for UL Yellow Card

SABIC

Availability

Asia Pacific

Uses

Appliances

Automotive Interior Parts

Automotive Under the Hood

Construction Applications

Decorative Parts

Electrical Parts

Electrical/Electronic Applications

Electronic Displays

Industrial Applications

Lighting Applications

Material Handling

Medical Devices

Medical/Healthcare Applications

Military/Defense Applications

Packaging

Water Management

Also Available In

Europe

Latin America

North America

PHYSICAL

Nominal Value

Unit

Test Method

Density / Specific Gravity

1.40

g/cm³

ASTM D792, ISO 1183Specific Volume

0.710

cm³/g

ASTM D792Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)

8.6

g/10 min

ASTM D1238Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)

8.0

cm³/10min

ISO 1133Molding Shrinkage

Internal MethodAcross Flow  3

0.90 to 1.9

%

Flow  3

1.1 to 1.8

%

Across Flow : 0.750 to 2.30 mm

1.0 to 1.7

%

Flow : 0.750 to 2.30 mm

0.90 to 1.6

%

Flow : 3.20 mm

1.5 to 2.3

%

Across Flow : 2.30 to 4.60 mm

1.6 to 2.4

%

Flow : 2.30 to 4.60 mm

1.5 to 2.3

%

Water Absorption

ISO 62Saturation, 23°C

0.36

%

Equilibrium, 23°C, 50% RH

0.080

%

MECHANICAL

Nominal Value

Unit

Test Method

Tensile Modulus


-- 4

2820

MPa

ASTM D638--

2800

MPa

ISO 527-1/1Tensile Strength


Yield 5

58.0

MPa

ASTM D638Yield

58.0

MPa

ISO 527-2/50Break 5

52.0

MPa

ASTM D638Break

40.0

MPa

ISO 527-2/50Tensile Elongation


Yield 5

5.0

%

ASTM D638Yield

5.0

%

ISO 527-2/50Break 5

18

%

ASTM D638Break

18

%

ISO 527-2/50Flexural Modulus


50.0 mm Span 6

2620

MPa

ASTM D790-- 7

2600

MPa

ISO 178Flexural Stress


-- 7, 8

90.0

MPa

ISO 178Yield, 50.0 mm Span 6

101

MPa

ASTM D790Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)

19.0

mg

Internal MethodIMPACT

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength


-30°C 9

4.0

kJ/m²

ISO 179/1eA23°C 9

8.0

kJ/m²

ISO 179/1eA23°C

5.0

kJ/m²

ISO 179/2CCharpy Unnotched Impact Strength 9

ISO 179/1eU-30°C

No Break

23°C

No Break

Notched Izod Impact


-30°C

25

J/m

ASTM D25623°C

40

J/m

ASTM D256-30°C 10

4.0

kJ/m²

ISO 180/1A23°C 10

5.0

kJ/m²

ISO 180/1AUnnotched Izod Impact


23°C

No Break

ASTM D4812, ISO 180/1U-30°C 10

No Break

ISO 180/1UInstrumented Dart Impact (23°C, Total Energy)

200

J

ASTM D3763HARDNESS

Nominal Value

Unit

Test Method

Rockwell Hardness (R-Scale)

120

ISO 2039-2Ball Indentation Hardness (H 358/30)

105

MPa

ISO 2039-1THERMAL

Nominal Value

Unit

Test Method

Deflection Temperature Under Load


0.45 MPa, Unannealed, 6.40 mm

162

°C

ASTM D6480.45 MPa, Unannealed, 4.00 mm, 100 mm Span 11

150

°C

ISO 75-2/Be1.8 MPa, Unannealed, 3.20 mm

74.0

°C

ASTM D6481.8 MPa, Unannealed, 6.40 mm

71.0

°C

ASTM D6481.8 MPa, Unannealed, 4.00 mm, 100 mm Span 11

60.0

°C

ISO 75-2/Ae1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10

73.0

°C

ISO 75-2/AfVicat Softening Temperature


--

170

°C

ASTM D1525 12, ISO 306/B120, ISO 306/B50--

212

°C

ISO 306/A50Ball Pressure Test (123 to 127°C)

Pass

IEC 60695-10-2CLTE


Flow : -40 to 40°C

7.9E-5

cm/cm/°C

ASTM E831Flow : 60 to 138°C

1.3E-4

cm/cm/°C

ASTM E831Flow : -40 to 40°C

7.6E-5

cm/cm/°C

ISO 11359-2Flow : 23 to 60°C

1.0E-4

cm/cm/°C

ISO 11359-2Transverse : -40 to 40°C

7.9E-5

cm/cm/°C

ASTM E831Transverse : -40 to 40°C

7.3E-5

cm/cm/°C

ISO 11359-2Transverse : 23 to 60°C

1.0E-4

cm/cm/°C

ISO 11359-2Thermal Conductivity

0.24

W/m/K

ISO 8302RTI Elec

120

°C

UL 746BRTI Imp

120

°C

UL 746BRTI Str

140

°C

UL 746BELECTRICAL

Nominal Value

Unit

Test Method

Surface Resistivity

> 1.0E+15

ohms

IEC 60093Volume Resistivity

> 1.0E+15

ohms·cm

IEC 60093Dielectric Strength


1.60 mm, in Oil

24

kV/mm

ASTM D1493.20 mm, in Air

18

kV/mm

ASTM D1490.800 mm, in Oil

35

kV/mm

IEC 60243-11.00 mm 13

18

kV/mm

IEC 60243-11.60 mm, in Oil

25

kV/mm

IEC 60243-13.20 mm, in Oil

17

kV/mm

IEC 60243-1Relative Permittivity

IEC 6025050 Hz

2.90

60 Hz

2.90

100 Hz

3.10

1 MHz

2.80

Dissipation Factor

IEC 6025050 Hz

1.0E-3

60 Hz

1.0E-3

100 Hz

2.0E-3

1 MHz

0.013

Arc Resistance 14

PLC 6

ASTM D495Comparative Tracking Index (CTI)

PLC 3

UL 746AComparative Tracking Index

IEC 60112--

175

V

Solution B

100

V

High Amp Arc Ignition (HAI) 15

PLC 0

UL 746AHigh Voltage Arc Resistance to Ignition (HVAR)

PLC 4

PLC 6

UL 746AHot-wire Ignition (HWI)

PLC 2

UL 746AFLAMMABILITY

Nominal Value

Unit

Test Method

Flame Rating

UL 940.71 mm

V-0

3.0 mm

5VA

Glow Wire Flammability Index (1.0 mm)

960

°C

IEC 60695-2-12Oxygen Index

30

%

ISO 4589-2INJECTION

Nominal Value

Unit

Drying Temperature

120

°C

Drying Time

3.0 to 4.0

hr

Suggested Max Moisture

0.020

%

Suggested Shot Size

40 to 80

%

Rear Temperature

230 to 250

°C

Middle Temperature

240 to 255

°C

Front Temperature

245 to 260

°C

Nozzle Temperature

240 to 255

°C

Processing (Melt) Temp

245 to 260

°C

Mold Temperature

50 to 75

°C

Back Pressure

0.300 to 0.700

MPa

Screw Speed

50 to 100

rpm

Vent Depth

0.013 to 0.025

mm

INJECTION NOTES

Drying Time (Cumulative): 12 hr

NOTES1A UL Yellow Card contains UL-verified flammability and electrical characteristics. UL Prospector continually works to link Yellow Cards to individual plastic materials in Prospector, however this list may not include all of the appropriate links. It is important that you verify the association between these Yellow Cards and the plastic material found in Prospector. For a complete listing of Yellow Cards, visit the UL Yellow Card Search.2Typical properties: these are not to be construed as specifications.3Tensile Bar45.0 mm/min5Type I, 50 mm/min61.3 mm/min72.0 mm/min8at Yield980*10*4 sp=62mm1080*10*4 mm11120*10*4 mm12Rate A (50°C/h), Loading 2 (50 N)13Shorttime14Tungsten Electrode15Surface