物理性能额定值 (公制)额定值 (英制)测试方法比重1.42 g/cc1.42 g/ccASTM D792密度1.42 g/cc0.0513 lb/in³ISO 1183Water Absorption0.30 %@Temperature 23.0 °C0.30 %@Temperature 73.4 °FImmersion 24h; ASTM D5701.0 %@Temperature 23.0 °C1.0 %@Temperature 73.4 °FSaturation, immersed; ISO 62, Similar to线性成型收缩率0.017 - 0.020 cm/cm@Thickness 3.20 mm0.017 - 0.020 in/in@Thickness 0.126 inTransverse, 24h; ASTM D9550.018 - 0.021 cm/cm@Thickness 3.20 mm0.018 - 0.021 in/in@Thickness 0.126 inFlow, 24h; ASTM D955线性模具收缩，Flow0.018 - 0.021 cm/cm@Thickness 4.00 mm0.018 - 0.021 in/in@Thickness 0.157 inParallel, 24h; ISO 294-40.021 cm/cm@Thickness 2.00 mm0.021 in/in@Thickness 0.0787 inISO 294-4线性成型收缩率,横向0.019 cm/cm@Thickness 2.00 mm0.019 in/in@Thickness 0.0787 inISO 294-40.018 - 0.021 cm/cm@Thickness 4.00 mmNormal, 24h; ISO 294-4熔体流动速率1.0 g/10 min@Load 1.05 kg, Temperature 190 °C1.0 g/10 min@Load 2.31 lb, Temperature 374 °FASTM D12382.4 g/10 min@Load 2.16 kg, Temperature 190 °C2.4 g/10 min@Load 4.76 lb, Temperature 374 °FISO 1133化合物熔体指数1.9 g/10 min@Load 2.16 kg, Temperature 190 °C1.9 g/10 min@Load 4.76 lb, Temperature 374 °Fcm3/10 min; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（M 级）9292ISO 2039/2洛氏硬度（R 级）120120ISO 2039/2121121ASTM D785抗张强度72.0 MPa@Temperature 23.0 °C10400 psi@Temperature 73.4 °F5mm/min (0.2in/min); ASTM D63860.799 MPa@Strain 2.8574 %, Temperature -40.0 °C8818.2 psi@Strain 2.8574 %, Temperature -40.0 °FISO 52787.176 MPa@Strain 5.7149 %, Temperature -40.0 °C12644 psi@Strain 5.7149 %, Temperature -40.0 °FISO 52794.877 MPa@Strain 8.5723 %, Temperature -40.0 °C13761 psi@Strain 8.5723 %, Temperature -40.0 °FISO 52796.84 MPa@Strain 11.43 %, Temperature -40.0 °C14050 psi@Strain 11.43 %, Temperature -40.0 °FISO 52797.432 MPa@Strain 14.287 %, Temperature -40.0 °C14131 psi@Strain 14.287 %, Temperature -40.0 °FISO 52797.672 MPa@Strain 17.145 %, Temperature -40.0 °C14166 psi@Strain 17.145 %, Temperature -40.0 °FISO 52798.055 MPa@Strain 20.002 %, Temperature -40.0 °C14222 psi@Strain 20.002 %, Temperature -40.0 °FISO 52798.733 MPa@Strain 22.86 %, Temperature -40.0 °C14320 psi@Strain 22.86 %, Temperature -40.0 °FISO 52799.053 MPa@Strain 25.717 %, Temperature -40.0 °C14366 psi@Strain 25.717 %, Temperature -40.0 °FISO 52799.549 MPa@Strain 28.574 %, Temperature -40.0 °C14438 psi@Strain 28.574 %, Temperature -40.0 °FISO 527抗张强度(屈服)72.0 MPa@Temperature 23.0 °C5mm/min (0.2in/min); ASTM D63872.0 MPa@Temperature 23.0 °CISO 527伸长率 (断裂)40 %@Temperature 23.0 °C40 %@Temperature 73.4 °Fnominal; ISO 52750 %@Temperature 23.0 °C50 %@Temperature 73.4 °FISO 52773 %@Temperature 23.0 °C73 %@Temperature 73.4 °F5mm/min (0.2in/min); ASTM D638Elongation at Yield20 %@Temperature 23.0 °C20 %@Temperature 73.4 °FISO 52721 %@Temperature 23.0 °C21 %@Temperature 73.4 °F5mm/min (0.2in/min); ASTM D638拉伸模量3.00 GPa@Temperature 23.0 °C435 ksi@Temperature 73.4 °F5mm/min (0.2in/min); ASTM D6383.20 GPa@Temperature 23.0 °C464 ksi@Temperature 73.4 °FISO 527弯曲强度80.0 MPa@Strain 3.50 %, Temperature 23.0 °C11600 psi@Strain 3.50 %, Temperature 73.4 °FISO 17892.0 MPa@Strain 5.00 %, Temperature 23.0 °C13300 psi@Strain 5.00 %, Temperature 73.4 °FASTM D790弯曲模量2.90 GPa@Temperature 23.0 °C421 ksi@Temperature 73.4 °FISO 1782.97 GPa@Temperature 23.0 °C431 ksi@Temperature 73.4 °FASTM D790悬壁梁缺口冲击强度0.960 J/cm@Temperature 23.0 °C1.80 ft-lb/in@Temperature 73.4 °FASTM D256悬壁梁无缺口冲击强度NB@Temperature 23.0 °CNB@Temperature 73.4 °FASTM D4812悬壁梁缺口冲击强度11.0 kJ/m²@Temperature -40.0 °C5.23 ft-lb/in²@Temperature -40.0 °FISO 180/1A11.0 kJ/m²@Temperature 23.0 °C5.23 ft-lb/in²@Temperature 73.4 °FISO 180/1A简支梁无缺口冲击强度27.0 J/cm²@Temperature -30.0 °C128 ft-lb/in²@Temperature -22.0 °FISO 179/1eU30.0 J/cm²@Temperature 23.0 °C143 ft-lb/in²@Temperature 73.4 °FISO 179/1eU简支梁缺口冲击强度0.900 J/cm²@Temperature -30.0 °C4.28 ft-lb/in²@Temperature -22.0 °FISO 179/1eA1.10 J/cm²@Temperature 23.0 °CISO 179/1eA拉伸蠕变模量(1 hr)3000 MPa@Temperature 23.0 °C435000 psi@Temperature 73.4 °FISO 899拉伸蠕变模量(1000 hr)1700 MPa@Temperature 23.0 °C247000 psi@Temperature 73.4 °FISO 899电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率8.00e+14 ohm-cm@Temperature 23.0 °C8.00e+14 ohm-cm@Temperature 73.4 °FASTM D257表面电阻6.00e+14 ohm@Temperature 23.0 °C6.00e+14 ohm@Temperature 73.4 °FASTM D257介电常数3.7@Frequency 1.00e+6 Hz, Temperature 23.0 °C3.7@Frequency 1.00e+6 Hz, Temperature 73.4 °FASTM D150介电强度18.0 kV/mm@Thickness 3.20 mm, Temperature 23.0 °C457 kV/in@Thickness 0.126 in, Temperature 73.4 °FShort Time; ASTM D149耗散因数0.0050@Frequency 1.00e+6 Hz, Temperature 23.0 °C0.0050@Frequency 1.00e+6 Hz, Temperature 73.4 °FASTM D150相比耐漏电起痕指数(CTI)600 V@Temperature 23.0 °C600 V@Temperature 73.4 °FIEC 60112600 V@Thickness 3.00 mm, Temperature 23.0 °C600 V@Thickness 0.118 in, Temperature 73.4 °FUL 746A热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动500 µm/m-°C@Temperature 23.0 - 55.0 °C278 µin/in-°F@Temperature 73.4 - 131 °FASTM E 831500 µm/m-°C@Temperature -40.0 - 23.0 °C278 µin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-2500 µm/m-°C@Temperature 23.0 - 55.0 °CISO 11359-1/-2500 µm/m-°C@Temperature 55.0 - 100 °C278 µin/in-°F@Temperature 131 - 212 °FISO 11359-1/-2线性热膨胀系数,横向流动94.0 µm/m-°C@Temperature -40.0 - 23.0 °C52.2 µin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-2110 µm/m-°C@Temperature 23.0 - 55.0 °C61.1 µin/in-°F@Temperature 73.4 - 131 °FASTM E 831110 µm/m-°C@Temperature 23.0 - 55.0 °CISO 11359-1/-2