基本性能额定值单位测试方法比重1.38g/cm³ASTM D792, ISO 1183熔体质量流动速率17g/10 minASTM D1238 (190℃/2.16kg)17g/10 minISO 1133成型收缩率 (flow)1.8 to 2.2%ASTM D955, ISO 294-4 (Across flow)1.8 to 2.2%ISO 294-4吸水率 (24hr)0.30%ASTM D570洛氏硬度ASTM D785 (M-Scale)81 (R-Scale)120机械性能额定值单位测试方法拉伸模量2800MPaISO 527-2拉伸应力 (Yield)60.0MPaISO 527-257.0MPaASTM D638拉伸伸长率 (Break)30%ASTM D638 (Break)40%ISO 527-2弯曲模量2650MPaASTM D790弯曲强度89.0MPaASTM D790夏比缺口冲击强度 (23°C)7.0kJ/m²ISO 179/1eAIZOD缺口冲击强度69.0J/mASTM D256热性能额定值单位测试方法热畸变温度 (0.45MPa,未退火)165°CASTM D648, ISO 75-2/B (1.8MPa,未退火)115°CASTM D648 (1.8MPa,未退火)100°CISO 75-2/A线性热膨胀系数 (flow)0.00010cm/cm/°CASTM E831其它性能额定值单位测试方法阻燃等级HBUL 94