SLOVASTER® B GF 30 FRK 3Polybutylene TerephthalatePlastcom30% 玻璃纤维增强材料产品说明：PBT with the content of 30 % chemically bound glass fibre and flame retardant based on red phosphorus. Anisotropy of shrinkage enables injection moulding of round, cylindric or other hole products. Application in engineering, electrical and automotive industry. High mechanical properties also in conditioned state. Delivered in natural mode and black colour.物性信息：基本信息填料/增强材料玻璃纤维增强材料, 30% 填料按重量添加剂阻燃性特性化学耦合阻燃性用途电气/电子应用领域工程配件汽车领域的应用外观黑色自然色加工方法注射成型树脂ID (ISO 1043)PBT物理性能额定值单位制测试方法密度1.66g/cm³ISO 1183熔流率（熔体流动速率） (250°C/2.16 kg)5.0g/10 minISO 1133收缩率STM 64 0808 垂直流动方向0.76%STM 64 0808 流动方向0.55%STM 64 0808含水量0.050%ISO 960机械性能额定值单位制测试方法拉伸模量9300MPaISO 527-2拉伸应力 (屈服)130MPaISO 527-2拉伸应变 (屈服)2.0%ISO 527-2弯曲模量10000MPaISO 178弯曲应力200MPaISO 178冲击性能额定值单位制测试方法简支梁缺口冲击强度ISO 179 -20°C7.0kJ/m²ISO 179 23°C7.0kJ/m²ISO 179简支梁无缺口冲击强度ISO 179 -20°C55kJ/m²ISO 179 23°C50kJ/m²ISO 179热性能额定值单位制测试方法热变形温度 (0.45 MPa, 未退火)210°CISO 75-2/B维卡软化温度210°CISO 306/B溶融温度（DSC）200 到 220°CISO 3146电气性能额定值单位制测试方法表面电阻率1.0E+15ohmsIEC 60093体积电阻率1.0E+17ohms·cmIEC 60093介电强度34kV/mmIEC 60243-1漏电起痕指数 (解决方案 A)225VIEC 60112可燃性额定值单位制测试方法UL 阻燃等级V-0UL 94热灯丝点火温度960°CIEC 注射额定值单位制干燥温度120°C干燥时间4.0hr加工（熔体）温度250 到 280°C模具温度50.0 到 90.0°C注塑压力60.0 到 100MPa