基本性能额定值单位测试方法比重1.41g/cm³ASTM D792, ISO 1183熔体质量流动速率13g/10 minASTM D792, ISO 1183成型收缩率 (flow,3.00MM)2.0%ASTM D955 (3.00mm)2.0%ISO 294-4吸水率 (E,23℃,60%rh)0.22%ASTM D570洛氏硬度 (M-Scale)82ASTM D785机械性能额定值单位测试方法拉伸强度 (Yield,23℃)65.0MPaASTM D638 (Yield,23℃)70.0MPaISO 527-2拉伸伸长率 (Break,23℃)55%ASTM D638 (Break,23℃)30%ISO 527-2弯曲模量 (23°C)2790MPaASTM D790 (23°C)2800MPaISO 178弯曲强度 (23°C)93.0MPaASTM D790 (23°C)94.0MPaISO 178剪切强度 (2.00mm)56.0MPaASTM D732夏比缺口冲击强度7.5kJ/m²ISO 179/1eAIZOD缺口冲击强度 (3.20mm)69.0J/mASTM D256电气性能额定值单位测试方法表面电阻率1.0E+16ohmsASTM D2571.0E+14ohmsIEC 60093体积电阻率1.0E+14ohm·cmASTM D2571.0E+12ohm·cmIEC 60093电气强度19kV/mmASTM D149, IEC 60243-1介电常数 (1E+6 Hz)3.70ASTM D150介质损耗因数 (1E+6 Hz)0.0070ASTM D150热性能额定值单位测试方法热畸变温度ASTM D648 (0.45MPa,未退火)158°C (1.8MPa,未退火)112°C (1.8MPa,未退火)110°C熔融温度165°CDSC线性热膨胀系数 (flow,20 to 80°C)0.00013cm/cm/°CASTM D696其它性能额定值单位测试方法阻燃等级 (0.8mm)HBUL 94