DuPont Performance Polymers Zytel® HTN 52G35HSL NC010 Polyphthalamide (PPA) 物性表物理性能额定值 (公制)额定值 (英制)测试方法比重1.47 g/cc1.47 g/ccDAM; ASTM D792密度1.45 g/cc0.0524 lb/in³DAM; ISO 1183填料含量35 %35 %DAM线性成型收缩率0.0025 cm/cm@Thickness 1.60 mm0.0025 in/in@Thickness 0.0630 inFlow; DAM0.0030 cm/cm@Thickness 3.20 mm0.0030 in/in@Thickness 0.126 inFlow; DAM0.010 cm/cm@Thickness 1.60 mm0.010 in/in@Thickness 0.0630 inTransverse; DAM0.010 cm/cm@Thickness 3.20 mm0.010 in/in@Thickness 0.126 inTransverse; DAM线性成型收缩率,Flow0.0020 cm/cm@Thickness 2.00 mm0.0020 in/in@Thickness 0.0787 inDAM; ISO 294-4机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（M 级）105105DAM; ASTM D785洛氏硬度（R 级）124124DAM; ASTM D785抗张强度(断裂)180 MPa@Temperature 23.0 °C26100 psi@Temperature 73.4 °F50%RH; ISO 527200 MPa@Temperature 23.0 °C29000 psi@Temperature 73.4 °FDAM; ISO 527抗张强度72.4 MPa@Temperature 200 °C10500 psi@Temperature 392 °FDAM; ASTM D63880.0 MPa@Temperature 175 °C11600 psi@Temperature 347 °FDAM; ASTM D63889.0 MPa@Temperature 150 °C12900 psi@Temperature 302 °FDAM; ASTM D638124 MPa@Temperature 100 °C18000 psi@Temperature 212 °FDAM; ASTM D638168 MPa@Temperature 23.0 °C24400 psi@Temperature 73.4 °F50%RH; ASTM D638188 MPa@Temperature 60.0 °C27300 psi@Temperature 140 °FDAM; ASTM D638204 MPa@Temperature 23.0 °C29600 psi@Temperature 73.4 °FDAM; ASTM D638230 MPa@Temperature -40.0 °C33400 psi@Temperature -40.0 °FDAM; ASTM D63821.57 MPa@Strain 0.210 %, Temperature 23.0 °C3128 psi@Strain 0.210 %, Temperature 73.4 °FDAM; ISO 11403-1/-223.46 MPa@Strain 0.510 %, Temperature 150 °C3403 psi@Strain 0.510 %, Temperature 302 °F50%RH; ISO 11403-1/-224.31 MPa@Strain 0.210 %, Temperature 0.000 °C3526 psi@Strain 0.210 %, Temperature 32.0 °FDAM; ISO 11403-1/-224.56 MPa@Strain 0.220 %, Temperature 40.0 °C3562 psi@Strain 0.220 %, Temperature 104 °FDAM; ISO 11403-1/-224.63 MPa@Strain 0.200 %, Temperature -20.0 °C3572 psi@Strain 0.200 %, Temperature -4.00 °FDAM; ISO 11403-1/-225.85 MPa@Strain 0.210 %, Temperature -20.0 °C3749 psi@Strain 0.210 %, Temperature -4.00 °F50%RH; ISO 11403-1/-226.02 MPa@Strain 0.510 %, Temperature 120 °C3774 psi@Strain 0.510 %, Temperature 248 °F50%RH; ISO 11403-1/-226.87 MPa@Strain 0.230 %, Temperature 0.000 °C3897 psi@Strain 0.230 %, Temperature 32.0 °F50%RH; ISO 11403-1/-227.0 MPa@Strain 0.520 %, Temperature 150 °C3920 psi@Strain 0.520 %, Temperature 302 °FDAM; ISO 11403-1/-229.31 MPa@Strain 0.270 %, Temperature 60.0 °C4251 psi@Strain 0.270 %, Temperature 140 °FDAM; ISO 11403-1/-229.53 MPa@Strain 0.260 %, Temperature 23.0 °C4283 psi@Strain 0.260 %, Temperature 73.4 °F50%RH; ISO 11403-1/-230.36 MPa@Strain 0.520 %, Temperature 90.0 °C4403 psi@Strain 0.520 %, Temperature 194 °F50%RH; ISO 11403-1/-231.33 MPa@Strain 0.480 %, Temperature 120 °C4544 psi@Strain 0.480 %, Temperature 248 °FDAM; ISO 11403-1/-233.66 MPa@Strain 0.430 %, Temperature 90.0 °C4882 psi@Strain 0.430 %, Temperature 194 °FDAM; ISO 11403-1/-2