基本性能额定值单位测试方法熔体流动速率33g/10minASTM D1238 (190℃/2.16kg)34g/10minISO 1133吸水率 (24 hr)0.2%ASTM D570物理性能额定值单位测试方法比重1.42g/cmASTM D792,ISO 1183成型收缩率 (Flow)1.7-2.1%ASTM D955,ISO 294-4 (Across Flow)1.7-2.1%ISO 294-4洛氏硬度ASTM D785 (M-Scale)94 (R-Scale)120机械性能额定值单位测试方法拉伸模量3400MPaISO 527-2屈服拉伸应力73MPaISO 527-2拉伸应力69MPaASTM D638断裂伸长率30%ASTM D63825%ISO 527-2弯曲模量3040MPaASTM D790弯曲强度106MPaASTM D790泰伯耐磨性 (1000 Cycles)13mgASTM D1044CHARPY缺口冲击强度 (23℃)6kJ/mISO 179/1eAIzod 缺口冲强度49J/mASTM D256热性能额定值单位测试方法热变形温度 (0.45MPa,unannealed)172℃ASTM D648 (0.45MPa,unannealed)165℃ISO 75-2/B (1.8MPa,unannealed)136℃ASTM D648 (1.8MPa,unannealed)100℃ISO 75-2/A流动方向线性热膨胀系数0.0001cm/cm/℃ASTM E831阻燃等级HBUL 94