Nylon 66
DuPont Performance Polymers
产品说明：
Zytel® E42A is a high viscosity polyamide 66 for injection molding and extrusion. It has improved break resistance for thick-walled parts.
Information provided by DuPont Performance Polymers
物性信息：
| 密度 | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 2.7 % @Temperature 23.0 °C | 2.7 % @Temperature 73.4 °F | E 50%RH; DAM; ISO 62, Similar to |
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |
| 粘度 | 109000 cP @Shear Rate 7000 1/s, Temperature 305 °C | 109000 cP @Shear Rate 7000 1/s, Temperature 581 °F | DAM; ISO 11443 |
| 119000 cP @Shear Rate 7000 1/s, Temperature 295 °C | 119000 cP @Shear Rate 7000 1/s, Temperature 563 °F | DAM; ISO 11443 | |
| 136000 cP @Shear Rate 5000 1/s, Temperature 305 °C | 136000 cP @Shear Rate 5000 1/s, Temperature 581 °F | DAM; ISO 11443 | |
| 144000 cP @Shear Rate 7000 1/s, Temperature 275 °C | 144000 cP @Shear Rate 7000 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| 150000 cP @Shear Rate 5000 1/s, Temperature 295 °C | 150000 cP @Shear Rate 5000 1/s, Temperature 563 °F | DAM; ISO 11443 | |
| 182000 cP @Shear Rate 5000 1/s, Temperature 275 °C | 182000 cP @Shear Rate 5000 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| 243000 cP @Shear Rate 2000 1/s, Temperature 305 °C | 243000 cP @Shear Rate 2000 1/s, Temperature 581 °F | DAM; ISO 11443 | |
| 274000 cP @Shear Rate 2000 1/s, Temperature 295 °C | 274000 cP @Shear Rate 2000 1/s, Temperature 563 °F | DAM; ISO 11443 | |
| 342000 cP @Shear Rate 2000 1/s, Temperature 275 °C | 342000 cP @Shear Rate 2000 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| 360000 cP @Shear Rate 1000 1/s, Temperature 305 °C | 360000 cP @Shear Rate 1000 1/s, Temperature 581 °F | DAM; ISO 11443 | |
| 413000 cP @Shear Rate 1000 1/s, Temperature 295 °C | 413000 cP @Shear Rate 1000 1/s, Temperature 563 °F | DAM; ISO 11443 | |
| 431000 cP @Shear Rate 700 1/s, Temperature 305 °C | 431000 cP @Shear Rate 700 1/s, Temperature 581 °F | DAM; ISO 11443 | |
| 501000 cP @Shear Rate 700 1/s, Temperature 295 °C | 501000 cP @Shear Rate 700 1/s, Temperature 563 °F | DAM; ISO 11443 | |
| 504000 cP @Shear Rate 500 1/s, Temperature 305 °C | 504000 cP @Shear Rate 500 1/s, Temperature 581 °F | DAM; ISO 11443 | |
| 535000 cP @Shear Rate 1000 1/s, Temperature 275 °C | 535000 cP @Shear Rate 1000 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| 593000 cP @Shear Rate 500 1/s, Temperature 295 °C | 593000 cP @Shear Rate 500 1/s, Temperature 563 °F | DAM; ISO 11443 | |
| 664000 cP @Shear Rate 700 1/s, Temperature 275 °C | 664000 cP @Shear Rate 700 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| 806000 cP @Shear Rate 500 1/s, Temperature 275 °C | 806000 cP @Shear Rate 500 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| 线性成型收缩率,Flow | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 抗张强度 | 13.4 MPa @Strain 3.00 %, Temperature 90.0 °C | 1940 psi @Strain 3.00 %, Temperature 194 °F | 50%RH; ISO 527 |
| 14.5 MPa @Strain 5.00 %, Temperature 120 °C | 2100 psi @Strain 5.00 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 15.9 MPa @Strain 3.00 %, Temperature 60.0 °C | 2310 psi @Strain 3.00 %, Temperature 140 °F | 50%RH; ISO 527 | |
| 17.6 MPa @Strain 5.00 %, Temperature 120 °C | 2550 psi @Strain 5.00 %, Temperature 248 °F | DAM; ISO 527 | |
| 19.7 MPa @Strain 3.00 %, Temperature 40.0 °C | 2860 psi @Strain 3.00 %, Temperature 104 °F | 50%RH; ISO 527 | |
| 20.9 MPa @Strain 10.0 %, Temperature 120 °C | 3030 psi @Strain 10.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 21.1 MPa @Strain 6.00 %, Temperature 90.0 °C | 3060 psi @Strain 6.00 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 21.8 MPa @Strain 5.00 %, Temperature 90.0 °C | 3160 psi @Strain 5.00 %, Temperature 194 °F | DAM; ISO 527 | |
| 22.4 MPa @Strain 0.800 %, Temperature 40.0 °C | 3250 psi @Strain 0.800 %, Temperature 104 °F | DAM; ISO 527 | |
| 23.5 MPa @Strain 10.0 %, Temperature 120 °C | 3410 psi @Strain 10.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 24.2 MPa @Strain 15.0 %, Temperature 120 °C | 3510 psi @Strain 15.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 24.8 MPa @Strain 6.00 %, Temperature 60.0 °C | 3600 psi @Strain 6.00 %, Temperature 140 °F | 50%RH; ISO 527 | |
| 24.9 MPa @Strain 0.800 %, Temperature 23.0 °C | 3610 psi @Strain 0.800 %, Temperature 73.4 °F | DAM; ISO 527 | |
| 25.8 MPa @Strain 9.00 %, Temperature 90.0 °C | 3740 psi @Strain 9.00 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 26.1 MPa @Strain 20.0 %, Temperature 120 °C | 3790 psi @Strain 20.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 26.3 MPa @Strain 15.0 %, Temperature 120 °C | 3810 psi @Strain 15.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 27.2 MPa @Strain 25.0 %, Temperature 120 °C | 3950 psi @Strain 25.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 27.2 MPa @Strain 3.00 %, Temperature 60.0 °C | 3950 psi @Strain 3.00 %, Temperature 140 °F | DAM; ISO 527 | |
| 27.9 MPa @Strain 30.0 %, Temperature 120 °C | 4050 psi @Strain 30.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 27.9 MPa @Strain 20.0 %, Temperature 120 °C | 4050 psi @Strain 20.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 28.2 MPa @Strain 35.0 %, Temperature 120 °C | 4090 psi @Strain 35.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 28.3 MPa @Strain 40.0 %, Temperature 120 °C | 4100 psi @Strain 40.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 28.4 MPa @Strain 45.0 %, Temperature 120 °C | 4120 psi @Strain 45.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 28.5 MPa @Strain 50.0 %, Temperature 120 °C | 4130 psi @Strain 50.0 %, Temperature 248 °F | 50%RH; ISO 527 | |
| 28.5 MPa @Strain 3.00 %, Temperature 23.0 °C | 4130 psi @Strain 3.00 %, Temperature 73.4 °F | 50%RH; ISO 527 | |
| 28.8 MPa @Strain 12.0 %, Temperature 90.0 °C | 4180 psi @Strain 12.0 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 28.9 MPa @Strain 25.0 %, Temperature 120 °C | 4190 psi @Strain 25.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 29.6 MPa @Strain 30.0 %, Temperature 120 °C | 4290 psi @Strain 30.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 29.6 MPa @Strain 10.0 %, Temperature 90.0 °C | 4290 psi @Strain 10.0 %, Temperature 194 °F | DAM; ISO 527 | |
| 30.0 MPa @Strain 35.0 %, Temperature 120 °C | 4350 psi @Strain 35.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 30.1 MPa @Strain 6.00 %, Temperature 40.0 °C | 4370 psi @Strain 6.00 %, Temperature 104 °F | 50%RH; ISO 527 | |
| 30.3 MPa @Strain 9.00 %, Temperature 60.0 °C | 4390 psi @Strain 9.00 %, Temperature 140 °F | 50%RH; ISO 527 | |
| 30.4 MPa @Strain 40.0 %, Temperature 120 °C | 4410 psi @Strain 40.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 30.6 MPa @Strain 45.0 %, Temperature 120 °C | 4440 psi @Strain 45.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 30.7 MPa @Strain 15.0 %, Temperature 90.0 °C | 4450 psi @Strain 15.0 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 30.7 MPa @Strain 50.0 %, Temperature 120 °C | 4450 psi @Strain 50.0 %, Temperature 248 °F | DAM; ISO 527 | |
| 31.9 MPa @Strain 18.0 %, Temperature 90.0 °C | 4630 psi @Strain 18.0 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 32.7 MPa @Strain 21.0 %, Temperature 90.0 °C | 4740 psi @Strain 21.0 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 33.1 MPa @Strain 24.0 %, Temperature 90.0 °C | 4800 psi @Strain 24.0 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 33.3 MPa @Strain 27.0 %, Temperature 90.0 °C | 4830 psi @Strain 27.0 %, Temperature 194 °F | 50%RH; ISO 527 | |
| 33.4 MPa @Strain 30.0 %, Temperature 90.0 °C | 4840 psi @Strain 30.0 %, Temperature 194 °F | 50%RH; ISO 527 |