热稳定 PA6 德国巴斯夫 8202HS BK102 抗化学 耐磨 用于家具 齿轮 紧固件
Polyamide 6
BASF Corporation
产品说明：
Ultramid 8202 HS BK-102 is an unreinforced, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses the combination of strength, stiffness and toughness properties as well as excellent chemical, thermal and abrasion resistance. The heat stabilizer system extends its retention of properties at elevated temperatures.
Applications
Ultramid 8202 HS BK-102 is generally recommended for applications such as drapery hardware, gears, fittings, furniture casters, bearings, handles, clips and fasteners.
物性信息：
| 添加剂 | 热稳定剂 |
| 特性 | 低粘度 刚性，良好 均聚物 良好的流动性 良好的强度 良好耐磨损性 耐化学性良好 耐热性，中等 热稳定性 韧性良好 通用 |
| 用途 | 把手 齿轮 家具 紧固件 配件 轴承 |
| 机构评级 | EC 1907/2006 (REACH) |
| RoHS 合规性 | RoHS 合规 |
| 外观 | 黑色 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 比重 | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 1.2 | -- | % | |
| 吸水率 | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| 饱和 | 9.5 | -- | % | ASTM D570 |
| 饱和, 23°C | 9.5 | -- | % | ISO 62 |
| 平衡, 50% RH | 2.7 | -- | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.7 | -- | % | ISO 62 |
| 洛氏硬度 (R 级) | 119 | -- | ASTM D785 |
| 拉伸模量 (23°C) | 3100 | 970 | MPa | ISO 527-2 |
| 抗张强度 (屈服, 23°C) | 85.0 | 36.0 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 | ||||
| 屈服, 23°C | 4.0 | 16 | % | ASTM D638, ISO 527-2 |
| 断裂, 23°C | 50 | > 100 | % | ASTM D638 |
| 标称拉伸断裂应变 (23°C) | 25 | > 50 | % | ISO 527-2 |
| 弯曲模量 | ||||
| 23°C | 2830 | -- | MPa | ASTM D790 |
| 23°C | 2650 | 770 | MPa | ISO 178 |
| 弯曲强度 | ||||
| 23°C | 108 | 35.0 | MPa | ASTM D790 |
| 23°C | 90.0 | 25.0 | MPa | ISO 178 |
| 简支梁缺口冲击强度 (23°C) | 3.0 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度 (23°C) | 无断裂 | -- | ISO 179 | |
| 悬壁梁缺口冲击强度 | ||||
| 23°C | 55 | -- | J/m | ASTM D256 |
| -40°C | 4.0 | -- | kJ/m² | ISO 180 |
| 23°C | 5.5 | -- | kJ/m² | ISO 180 |
| 载荷下热变形温度 | ||||
| 0.45 MPa, 未退火 | 178 | -- | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 65.0 | -- | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 60.0 | -- | °C | ISO 75-2/A |
| 熔融峰值温度 | 220 | -- | °C | ASTM D3418, ISO 3146 |
| 线形热膨胀系数 - 流动 | 8.3E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | UL 746 |
| 1.50 mm | 130 | -- | °C | UL 746 |
| 3.00 mm | 130 | -- | °C | UL 746 |
| 6.00 mm | 130 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | UL 746 |
| 1.50 mm | 105 | -- | °C | UL 746 |
| 3.00 mm | 105 | -- | °C | UL 746 |
| 6.00 mm | 105 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | UL 746 |
| 1.50 mm | 105 | -- | °C | UL 746 |
| 3.00 mm | 105 | -- | °C | UL 746 |
| 6.00 mm | 105 | -- | °C | UL 746 |
热稳定 PA6 德国巴斯夫 8202HS BK102 抗化学 耐磨 用于家具 齿轮 紧固件