耐碳氢化合物 Ultramid® 8231GHS 德国巴斯夫 PA66 安全帽 齿轮 高温应用
Polyamide 6
BASF Corporation
15% 玻璃纤维增强材料
产品说明：
Ultramid 8231G HS is a heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
物性信息：
| 黄卡编号 | E |
| 填料/增强材料 | 玻璃纤维增强材料, 15% 填料按重量 |
| 添加剂 | 热稳定剂 |
| 特性 | 刚性，良好 良好的强度 耐化学性良好 耐碳氢化合物 耐油性能 耐油脂性能 热稳定性 |
| 用途 | 安全帽 齿轮 垫圈 高温应用 汽车领域的应用 |
| 机构评级 | EC 1907/2006 (REACH) |
| RoHS 合规性 | RoHS 合规 |
| 外观 | 可用颜色 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 比重 | 1.23 | -- | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 0.50 | -- | % | |
| 吸水率 | ||||
| 24 hr | 1.4 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.4 | -- | % | ISO 62 |
| 饱和 | 8.1 | -- | % | ASTM D570 |
| 饱和, 23°C | 8.1 | -- | % | ISO 62 |
| 平衡, 50% RH | 2.3 | -- | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| 洛氏硬度 (R 级) | 121 | -- | ASTM D785 |
| 拉伸模量 | ISO 527-2 | |||
| -40°C | 5950 | 6600 | MPa | ISO 527-2 |
| 23°C | 5960 | 2640 | MPa | ISO 527-2 |
| 80°C | 2470 | 2300 | MPa | ISO 527-2 |
| 121°C | 2090 | 1900 | MPa | ISO 527-2 |
| 抗张强度 | ||||
| 断裂, -40°C | 160 | 170 | MPa | ASTM D638, ISO 527-2 |
| 断裂, 23°C | 140 | 79.0 | MPa | ASTM D638 |
| 断裂, 80°C | 60.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| 断裂, 121°C | 50.0 | 40.0 | MPa | ASTM D638, ISO 527-2 |
| 断裂, 23°C | 140 | 80.0 | MPa | ISO 527-2 |
| 断裂, -40°C | 3.0 | 4.0 | % | ASTM D638 |
| 断裂, 23°C | 4.0 | 9.0 | % | ASTM D638, ISO 527-2 |
| 断裂, 80°C | 8.0 | 15 | % | ASTM D638 |
| 断裂, 121°C | 7.0 | 6.0 | % | ASTM D638 |
| 弯曲模量 | ||||
| -40°C | 5860 | 6430 | MPa | ASTM D790 |
| 23°C | 5310 | 2400 | MPa | ASTM D790 |
| 65°C | 2400 | -- | MPa | ASTM D790 |
| 121°C | 1930 | -- | MPa | ASTM D790 |
| 23°C | 4770 | 2210 | MPa | ISO 178 |
| 弯曲强度 | ||||
| -40°C | 214 | 219 | MPa | ASTM D790 |
| 23°C | 172 | 101 | MPa | ASTM D790 |
| 65°C | 110 | -- | MPa | ASTM D790 |
| 90°C | 90.0 | -- | MPa | ASTM D790 |
| 121°C | 76.0 | -- | MPa | ASTM D790 |
| 23°C | 160 | 65.0 | MPa | ISO 178 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30°C | 5.5 | -- | kJ/m² | ISO 179 |
| 23°C | 6.5 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度 (23°C) | 40 | -- | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度 | ||||
| 23°C | 59 | -- | J/m | ASTM D256 |
| 23°C | 5.0 | -- | kJ/m² | ISO 180 |
耐碳氢化合物 Ultramid® 8231GHS 德国巴斯夫 PA66 安全帽 齿轮 高温应用
8231GHS ,德国巴斯夫 PA66,耐碳氢化合物pa66,高强度pa66,增强级pa66