Aerospace Lubricants 15

Aerospace Lubricants Tribolube 15 Grease These greases are especially useful in vacuum and other systems where non-reactivity with chemicals, strong acids and oxidizers, fuels, and solvents is re Each grease is suited for different operating environment temperatures. Although this lubricant is very inert, newly exposed rubbing surfaces of aluminum and magnesium may react with the greases under certain conditions.

Approvals/References/Specification

US Military Specification: MIL-G-27617D

US Military Specification: MIL-PRF-27617 Type 4

Type of Lubricant: Fluorinated Polyether Grease

Packaging: 2-Oz. Tube

NLGI No.: 2

Temperature Range: -100 to 450 °F

Unworked Penetration @ 77°F: 291

Worked Penetration @ 60 Strokes: 295

Evaporation 22 hrs @ 400°F: 4.31 %

Weld Point @ Load: 800 kg

Copper Corrosion 24 hrs @ 212°F: 1b

Evaporation 30 hrs @ 400°F: 4.51 %

Oil Separation 30 hrs @ 400°F: 9.66 %

Oil Separation 30 hrs @ 450°F: 10.24 %

LOX Impact Sensitivity 20 impacts from 43.3 in: No Reaction

Load Wear Index: 170.29

Last Non-Seizure @ Load/Wear Scar: 80/0.52 kg/mm

Last Seizure @ Load/Wear Scar: 600/1.71 kg/mm

Steel-on-Steel Wear @ 1200 rpm. 40 kg. 167°F. 1 hrs. 52100 steel: 0.70 mm

Steel-on-Steel Wear @ 1200 rpm. 40 kg. 400°F. 1 hrs. 52100 steel: 1.12 mm

High Temperature Performance @ 450°F. 10000 rpm. 5 lbs: 500+ hrs

High Temperature Performance @ 400°F. 10000 rpm. 5 lbs: 1600+ hrs

Low Temperature Torque @-100°F. Starting: 1,450 gm-cm

Low Temperature Torque @-100°F. 60 min. Running: 618 gm-cm

Low Temperature Torque @-65°F. Starting: 520 gm-cm

Low Temperature Torque @-65°F. Running: 163 gm-cm

Film Stability and Steel Corrosion 168 hrs @ 212°F: Pass

Mil Specs: MIL-G-27617, MIL-G-27617D, MIL-PRF-27617, MIL-PRF-27617 (Type 4)

Type: 15