| 性能项目 | 测试条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 性能 | 拉伸强度 | ASTM D638 |
| 16.4 113 | kpsi Mpa |
| 拉伸模量 | ASTM D638 |
| 990 6.8 | kpsi GPa |
| 拉伸伸长率 | ASTM D638 |
| 3.3 | % |
| 挠曲强度 | ASTM D790 |
| 31.2 215 | kpsi Mpa |
| 挠曲模量 | ASTM D790 |
| 1000 6.9 | kpsi GPa |
| 压缩强度 | ASTM D695 |
| 24.1 166 | kpsi Mpa |
| 剪切强度 | ASTM D732 |
| 16.1 111 | kpsi Mpa |
| 比重 | ASTM D 792 |
| 1.46 |
|
| 吸水性，24小时 | ASTM D 570 |
| 0.28 | % |
| 热变形温度 | 264psi,ASTM D 648 |
| 279 534 | ℃ ℉ |
| 体积电阻率 | ASTM D 257 |
| 8X1015 | ohm-cm |
| 摩擦系数，干摩擦50fpm（0.25m/s) | ASTM D 3702 |
| 0.31 |
|
| 摩擦系数，干摩擦800fpm(4m/s) | ASTM D 3702 |
| 0.39 |
|
| 摩损系数，干摩擦350fpm（0.25m/s) | ASTM D 3702 |
| 14 24 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| 摩损系数，干摩擦3800fpm(4m/s) | ASTM D 3702 |
| 17 30 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| 摩损系数，润滑环境4 | ASTM D 3702 |
|
| 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| 悬臂梁式冲击，有缺口 | ASTM D256 |
| 1.2 64 | ft-lb/in J/m |
| 悬臂梁式冲击，无缺口 | ASTM D4812 |
| 8 410 | ft-lb/in J/m |
| CLTE3 | ASTM D 696 |
| 25 14 | ppm/℃ ppm/℉ |