流动性能好的PC LEXAN HF1130R
PC 基础创新塑料(美国) HF1130R，LEXAN HF1130R Resin SABIC Innovative Plastics PC，添加脱模剂，紫外线稳定剂，性能特点：流动性高，抗紫外线。用途：薄壁部件。物理性能：比重1.20，溶指(300℃/1.2kg)25g/10min，收缩率0.5-0.7%，23℃悬臂冲击强度640J/M，热变形温度127℃，透射率(2540um)88%，雾度(2540um)1.0%，加工熔体温度271-293℃，干燥温度121℃。
物理性能：
Specific Gravity 1.20 g/cc 1.20 g/cc ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm 0.0050 - 0.0070 in/in
@Thickness 0.126 in SABIC Method
Melt Flow 25 g/10 min
@Load 1.20 kg,
Temperature 300 °C 25 g/10 min
@Load 2.65 lb,
Temperature 572 °F ASTM D1238
机械性能：
Tensile Strength at Break 65.0 MPa 9430 psi Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 62.0 MPa 8990 psi Type I, 50 mm/min; ASTM D638
Elongation at Break 110 % 110 % Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 % 6.0 % Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.37 GPa 344 ksi 5 mm/min; ASTM D638
Flexural Yield Strength 93.0 MPa 13500 psi 1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.30 GPa 334 ksi 1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.40 J/cm 12.0 ft-lb/in ASTM D256
Tensile Impact Strength 378 kJ/m² 180 ft-lb/in² Type S; ASTM D1822
Dart Drop, Total Energy 54.0 J 39.8 ft-lb Instrumented Impact Energy @ peak; ASTM D3763