20%玻璃微珠增强尼龙66 美国液氮 RB004
PA66 美国液氮 RB004
Eurostar Staramide RB004 PA66, 20% Glass Bead Filled, Injection Molded
Staramide RB004 是 20%玻璃微珠增强聚酰胺 66 注射成型树脂
SABIC Innovative Plastics LNP THERMOCOMP RB004 PA 66
LNP THERMOCOMP* RB004是一种基于尼龙66树脂含20 ％玻璃珠的化合物。
物理性能：
Specific Gravity 1.29 g/cc 1.29 g/cc ASTM D792
Density 1.28 g/cc 0.0462 lb/in³ ASTM D792
Moisture Absorption 0.620 % 0.620 % 50% RH, 24 hrs; ASTM D570
1.10 % 1.10 % 23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm
@Time 86400 sec >= 0.020 in/in
@Time 24.0 hour ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm
@Time 86400 sec 0.010 - 0.030 in/in
@Time 24.0 hour ASTM D955
机械性能：
Tensile Strength at Break 75.0 MPa 10900 psi 5 mm/min; ISO 527
80.0 MPa 11600 psi Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 79.0 MPa 11500 psi 5 mm/min; ISO 527
Elongation at Break 3.7 % 3.7 % Type I, 5 mm/min; ASTM D638
3.9 % 3.9 % 5 mm/min; ISO 527
Elongation at Yield 3.8 % 3.8 % 5 mm/min; ISO 527
Tensile Modulus 3.96 GPa 574 ksi 1 mm/min; ISO 527
4.10 GPa 595 ksi 50 mm/min; ASTM D638
Flexural Strength 119 MPa 17300 psi ISO 178
Flexural Modulus 3.70 GPa 537 ksi 2 mm/min; ISO 178
3.87 GPa 561 ksi 1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.280 J/cm 0.525 ft-lb/in ASTM D256
Izod Impact, Unnotched 2.27 J/cm 4.25 ft-lb/in ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m² 1.90 ft-lb/in² 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 16.0 kJ/m² 7.61 ft-lb/in² 80*10*4; ISO 180/1U
Dart Drop, Total Energy 2.00 J
@Temperature 23.0 °C 1.48 ft-lb
@Temperature 73.4 °F ASTM D3763