PEEK LC-1006沙伯基础

沙伯基础LC-1006属于聚醚醚酮碳纤维增强材料，聚合物，热塑性塑料，聚酮，聚醚醚酮（PEEK），聚醚酮，PEEK，碳纤维填充
Forms: Pellets
Processing Method: Injection Molding
Information provided by LNP, a GE Plastics Company.
This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase

物理性能 额定值 (公制) 额定值 (英制) 测试方法

比重	1.41 g/cc	1.41 g/cc	Method A; ASTM D792
线性成型收缩率	0.0010 cm/cm	0.0010 in/in	ASTM D955
线性成型收缩率，横向	0.0040 cm/cm	0.0040 in/in	ASTM D955

机械性能 额定值 (公制) 额定值 (英制) 测试方法

抗张强度(断裂)	225 MPa	32600 psi	ASTM D638
抗张强度(屈服)	225 MPa	32600 psi	ASTM D638
伸长率 (断裂)	1.5 %	1.5 %	ASTM D638
屈服伸长率	1.4 %	1.4 %	ASTM D638
拉伸模量	30.8 GPa	4470 ksi	ASTM D638
弯曲强度	324 MPa	47000 psi	ASTM D790
弯曲模量	20.2 GPa	2930 ksi	ASTM D790
悬壁梁缺口冲击强度	0.747 J/cm @Thickness 3.18 mm	1.40 ft-lb/in @Thickness 0.125 in	ASTM D256
悬壁梁无缺口冲击强度	6.09 J/cm @Thickness 3.18 mm	11.4 ft-lb/in @Thickness 0.125 in	ASTM D256
悬壁梁缺口冲击强度	7.80 kJ/m²	3.71 ft-lb/in²	ISO 180
悬壁梁无缺口冲击强度	42.6 kJ/m²	20.3 ft-lb/in²	ISO 180
Falling Dart Impact	12.5 J	9.22 ft-lb	ASTM D3763
动态摩擦系数	0.30	0.30	vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
静态摩擦系数	0.32	0.32	vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor	111 x 10-8 mm³/N-M	55.0 x 10-10 in³-min/ft-lb-hr	40psi, 50ft/min; tested in accordance with LNP WI-0687

热性能 额定值 (公制) 额定值 (英制) 测试方法

线性热膨胀系数	11.0 µm/m-°C @Temperature 20.0 °C	6.11 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
线性热膨胀系数,横向流动	29.0 µm/m-°C @Temperature 20.0 °C	16.1 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
载荷下热变形温度(0.46 MPa)	299 °C	570 °F	Unannealed; ASTM D648
载荷下热变形温度(1.8 MPa)	299 °C	570 °F	Unannealed; ASTM D648
可燃性(UL94)	V-0 @Thickness 0.770 mm	V-0 @Thickness 0.0303 in

加工性能 额定值 (公制) 额定值 (英制) 测试方法

加工（熔体）温度	°C	°F
模具温度	°C	°F
干燥温度	°C	°F
干燥时间	4 hour	4 hour
水分含量	0.10 %	0.10 %	Suggested
背压	0.345 - 0.689 MPa	50.0 - 99.9 psi