拜耳防火灰色PC材料|模科隆2205，拜耳防火PC，模科隆2205，PC防火，高熔指PC


Physical Properties Metric English Comments Mechanical Properties Metric English Comments

Bulk Density	0.660 g/cc	0.0238 lb/in³	pellets; ISO 60
Density	1.19 g/cc	0.0430 lb/in³	ISO 1183-1
Moisture Absorption at Equilibrium	0.12 %	0.12 %	Equilibrium at 50% RH; ISO 62
Water Absorption at Saturation	0.30 %	0.30 %
Water Vapor Transmission	15.0 g/m²/day	0.966 g/100 in²/day	85 % RH; 100 µm film; ISO 15106-1
Oxygen Transmission	750 cc-mm/m²-24hr-atm	1910 cc-mil/100 in²-24hr-atm	[cm³/(m²·24 h·bar)], 100 µm film; b.o. ISO 2556
	3150 cc-mm/m²-24hr-atm	8000 cc-mil/100 in²-24hr-atm	[cm³/(m²·24 h·bar)], 25.4 µm (1 mil) film; b.o. ISO 2556
Nitrogen Transmission	150 cc-mm/m²-24hr-atm	381 cc-mil/100 in²-24hr-atm	[cm³/(m²·24 h·bar)], 100 µm film; b.o. ISO 2556
	630 cc-mm/m²-24hr-atm	1600 cc-mil/100 in²-24hr-atm	[cm³/(m²·24 h·bar)], 25.4 µm (1 mil) film; b.o. ISO 2556
Carbon Dioxide Transmission	4500 cc-mm/m²-24hr-atm	11400 cc-mil/100 in²-24hr-atm	[cm³/(m²·24 h·bar)], 100 µm film; b.o. ISO 2556
	18900 cc-mm/m²-24hr-atm	48000 cc-mil/100 in²-24hr-atm	[cm³/(m²·24 h·bar)], 25.4 µm (1 mil) film; b.o. ISO 2556
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	b.o. ISO 25777
Linear Mold Shrinkage, Flow	0.0065 cm/cm	0.0065 in/in	60x60x2 mm; 500 bar; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0065 cm/cm	0.0065 in/in	60x60x2 mm; 500 bar; ISO 294-4
Melt Flow	37 g/10 min @Load 1.20 kg, Temperature 300 °C	37 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133
Puncture Resistance	4900 N @Temperature 23.0 °C	1100 lb (f) @Temperature 73.4 °F	ISO 6603-2
	5900 N @Temperature -30.0 °C	1330 lb (f) @Temperature -22.0 °F	ISO 6603-2
Ball Indentation Hardness	115 MPa	16700 psi	ISO 2039-1
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527-1,-2
Tensile Strength, Yield	65.0 MPa	9430 psi	50 mm/min; ISO 527-1,-2
Elongation at Break	>= 50 %	>= 50 %	Nominal, 50 mm/min; ISO 527-1,-2
	120 %	120 %	50 mm/min; ISO 527-1,-2
Elongation at Yield	6.0 %	6.0 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	2.40 GPa	348 ksi	1 mm/min; ISO 527-1,-2
Flexural Strength	97.0 MPa	14100 psi	2 mm/min; ISO 178
Flexural Yield Strength	73.0 MPa	10600 psi	at 3.5% strain; 2 mm/min; ISO 178
Flexural Modulus	2.35 GPa	341 ksi	2 mm/min; ISO 178