Basic knowledge of PPO modification
Without modification of polyphenylene oxide (PPO) resin has good mechanical properties, electrical property, heat resistance, flame retardancy, and chemical stability, etc., but its poor solvent resistance and products are prone to stress cracking, the notched impact strength is low, and it is a fatal weakness, melt viscosity, high processing formability is poor, cannot adopt pure PPO resin injection molding, which greatly limits its application.
供应加纤PPO,G701H,G702H,G703H，日本旭化成 阻燃HB；
供应加纤PPO+10GF, G701H，日本旭化成 阻燃HB；
供应加纤PPO+20GF, G702H，日本旭化成 阻燃HB；
供应加纤PPO+30GF, G703H，日本旭化成 阻燃HB；
供应加纤PPO,G701V,G702V,G703V，日本旭化成 阻燃V1；￥28,
供应加纤PPO+10GF, G701V，日本旭化成 阻燃V1；
供应加纤PPO+20GF, G702V，日本旭化成 阻燃V1；
PPO.340Z主要性能:阻燃性能。主要参数:密度:1.08g/cm3，吸水率:0.10%，成型收缩率:0.6%，断裂伸长率:40%，缺口冲击强度:15;
PPO.500V主要性能:阻燃性能。主要参数:密度:1.08g/cm3，吸水率:0.10%，成型收缩率:0.6%，断裂伸长率:40%，缺口冲击强度:15;
PPO.540V主要性能:阻燃性能。主要参数:密度:1.08g/cm3，吸水率:0.10%，成型收缩率:0.6%，断裂伸长率:40%，缺口冲击强度:15;
511主要性能:10%玻纤增强。主要参数:密度:1.16g/cm3，吸水率:0.10%，成型收缩率:0.6%，断裂伸长率:5.0%，缺口冲击强度:11;
50V主要性能:润滑剂，经润滑。主要参数:密度:1.08g/cm3，吸水率:0.10%，成型收缩率:0.55%，断裂伸长率:80%，缺口冲击强度:16;
702H主要性能:20%玻纤。主要参数:密度:1.20g/cm3，吸水率:0.06%，成型收缩率:0.3%，断裂伸长率:5.0%，缺口冲击强度:8.0;
703V主要性能:30%玻纤，阻燃性能。主要参数:密度:1.30g/cm3，吸水率:0.06%，成型收缩率:0.20%，断裂伸长率:5.0%，缺口冲击强度:8.0;
543V主要性能:30%未***填料\增强材料，流动性高。主要参数:密度:1.32g/cm3，吸水率:
0.06%，成型收缩率:0.35%，断裂伸长率:4.0%，缺口冲击强度:5.0;
544V主要性能:40%未***填料\增强材料，流动性高。主要参数:密度:1.43g/cm3，吸水率:
0.06%，成型收缩率:0.35%，断裂伸长率:3.0%，缺口冲击强度:5.0;
800主要性能:耐热性高。主要参数:密度:1.10g/cm3，吸水率:0.06%，成型收缩率:0.9%，断裂伸长率:70%，缺口冲击强度:18;
502主要参数:密度:1.22g/cm3，吸水率:0.06%，成型收缩率:0.5%，断裂伸长率:5.0%，缺口冲击强度:7.0;
成型性能 1.非结晶料,吸湿小。
2.流动性差，为类似牛顿流体，粘度对温度比较敏感，制品厚度一般在0.8毫米以上。极易分解，分解时产生腐蚀气体。宜严格控制成型温度，模具应加热，浇注系统对料流阻力应小。
3、聚苯醚的吸水率很低0.06％左右，但微量的水分会导致产品表面出现银丝等不光滑现象，是作干燥处理，温度不可高出150度，否则颜色会变化。
4、聚苯醚的成型温度为280-330度，改性聚苯醚的成型温度为260-285度。
优点：1、具良加工安定性；2、机械性能优异；3、耐热性高；4、具自熄性；5、耐水性良好;
6、电气特性佳；7、成形收缩率小；8、抗化学药品性好。