PC合金树脂PC-385 台湾奇美PC-385 PC/ABS一般成型制品 注塑级
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||
| 物理性能 | 吸水率 | 23,24hrs | ASTM D570 | 0.4 | |||
| 成型收缩率 | ASTM D955 | 0.4-0.6 | |||||
| 螺旋流动长度 | 260,2×4.8mm | CHIMEI | 83 | mm | |||
| 流动系数 | 260,3.8kg | ASTM D1238 | 13 | g/10min | |||
| 比重 | ASTM D792 | 1.14 | |||||
| 机械性能 | 弯曲模量 | 23 | ASTM D790 | 23500 | kg/cm2 | ||
| Izod缺口冲击强度 | 1/8″ | ASTM D256 | 65 | Kg.cm/cm | |||
| 延伸率 | 23 | ASTM D638 | 90 | ||||
| 引张强度 | 23 | ASTM D638 | 540 | kg/cm2 | |||
| 弯曲强度 | 23 | ASTM D790 | 800 | kg/cm2 | |||
| 热性能 | 阻燃性 | UL94 | HB | ||||
| 线膨胀系数 | 40-100 | ASTM D696 | 6-8 | ×105cm/cm/ | |||
| 软化点温度 | ASTM D1525 | 139 | |||||
| 热变形温度 | 未退火,1.82MPa | ASTM D648 | 108 | ||||