粉状Torlon AI-10 LM Solvay PAI 良好粘结性

Torlon? AI-10

聚酰胺-酰亚胺

Solvay Specialty Polymers

Product Description:

Torlon? AI-10 is a polyamideimide (PAI) powder developed for the performance coatings industry. As a liquid polymer solution, the resin is incorporated into the formulation of engineered coatings; often as the principal primer, binder, or high temperature adhesive component. As a powder, the resin is used in specialty composites and unique dry spray applications.

Torlon AI-10 LM Solvay PAI：

Coatings based on the Torlon? AI-10 polymer yield durable, abrasion resistant, thermally stable films that do not exhibit unwanted thermoplastic properties. The resin has superior resistance to organic solvents and a wide array of other commercial and industrial chemicals. Outstanding tribological characteristics are afforded both by the resin as well as its unparalleled intra-coat adhesion to fluoropolymers. Coatings based on AI-10 polymer have been shown to be cost effective in electrical/electronic, high temperature decorative and corrosion preventative applications.

Torlon AI-10 LM Solvay PAI：

Magnet wire insulation and protective coatings for printed circuit boards are some of the electrical uses. Industrial applications include primers and decorative topcoats for cookware, appliances and housewares. AI-10 polymer has been combined with fluoropolymers to produce high-performance, low-friction, corrosion-resistant coatings that provide protection to saw blades, gears, carburetor needles and lawn and garden tools. Torlon AI-10 is also used for high-strength, high-temperature adhesives. Excellent bond strengths have been observed with stainless steel, aluminum and titanium alloys and polyimide films.

A special grade (called AI-10 LM) has been developed to reduce the amount of residual methylene dianline (MDA) monomer to below the 1000ppm level specified in hazard communication regulations.

Torlon AI-10 LM Solvay PAI：

A water soluable analog of AI-10 (called Torlon? AI-30) is also available.

属性
加工方式
资料
视觉搜索
曲线数据
购买地点

Torlon AI-10 LM Solvay PAI：

总体
材料状态	已商用：当前有效
资料 1	Processing - Design Guide (English) Processing - Injection (English) Technical Datasheet
搜索 UL 黄卡	Solvay Specialty Polymers Torlon?
供货地区	北美洲非洲和中东拉丁美洲欧洲亚太地区
特性	良好粘结性耐化学品性能，良好耐磨损性，良好耐热性，高阻燃性
用途	涂层应用粘合剂粘合剂
RoHS 合规性	RoHS 合规
形式	粉状
加工方法	溶液处理涂层

物理性能	额定值	单位制
粘度 2 (23°C)	1.00	Pa·s

补充信息

额定值

单位制

不挥发物含量 3

Solubility
Torlon AI-10 resin is supplied as a powder that is readily dissolved in N-methyl pyrrolidone (NMP) and other aprotic solvents. Other organic solvents may be used as diluents to reduce viscosity at lower cost. N-methyl pyrrolidone is hydrophilic, and as such, retains considerable amounts of water. Adding non-polar diluents may be appropriate to aid in the application process and to prevent potential formulation and shelf stability issues.

Pigments and Additives
Pigments and additives can be used with Torlon AI-10 polymer to produce special purpose coating and adhesive formulations. Suitable additives include heat-stable organic and inorganic pigments, fillers and certain epoxy and fluoropolymer copolymers. Due to the inherent color of Torlon AI-10 polymer, care must be taken if white or very pale shades are to be successfully formulated. To prevent the absorption of unwanted moisture, all pigments should be ground in closed milling equipment. Likewise, hydroscopic additives, such as fibers and copolymers, should be dried to appropriate moisture levels prior to being incorporated into the formulation.

Application.
Depending on the aesthetic and performance characteristics required, uniform coatings can be applied by spray, roll, spin or curtain techniques. Usually, dry film thicknesses from 10-20 ?m are readily achieved in a single coating pass, with multicoat systems affording the opportunity for additional surface build. Regardless of the method employed, it is essential to assure appropriate preparation of the substrate prior to application of coating. once complete, application equipment should be purged of coating and cleaned with a true solvent.

Drying/Curing
Coatings based upon
Torlon AI-10 LM Solvay PAI： resin dry and initiate cure at temperatures as low as 150°C (300°F). However, optimal film properties result after heating for 5 to 20 minutes, depending on the film thickness and the formulation, at 250°C (480°F). In the case of multi-coat systems, an intermediate temperature step at around 200°C (390°F) for 10 minutes may be advisable. For coating formulations employing low solids, a brief flash off period of about 3 to 10 minutes may be recommended prior to initiating cure.