PC沙伯基础503R-131耐候高刚性阻燃加纤10%防火V0级内润滑高韧性

LEXAN™ 503R resinPolycarbonateSABIC Innovative Plastics10% 玻璃纤维增强材料产品说明：10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release.物性信息：基本信息黄卡编号填料/增强材料添加剂特性加工方法注射成型刚性，高抗撞击性，良好阻燃性脱模紫外线稳定剂玻璃纤维增强材料, 10% 填料按重量E121562-220888物理性能额定值单位制测试方法比重1.25g/cm³ASTM D792特定体积0.802cm³/gASTM D792收缩率 - 流动 (3.20 mm)0.20 到 0.40%内部方法吸水率ASTM D570    24 hr0.12%ASTM D570    平衡, 23°C0.31%ASTM D570室外适用性f1UL 746C硬度额定值单位制测试方法洛氏硬度ASTM D785    M 级85ASTM D785    R 级124ASTM D785机械性能额定值单位制测试方法抗张强度 1ASTM D638    屈服66.2MPaASTM D638    断裂55.2MPaASTM D638伸长率 2ASTM D638    屈服8.0%ASTM D638    断裂15%ASTM D638弯曲模量 3(50.0 mm 跨距)3450MPaASTM D790弯曲强度 4(屈服, 50.0 mm 跨距)103MPaASTM D790泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)11.0mgASTM D1044冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°C)110J/mASTM D256无缺口悬臂梁冲击 (23°C)2100J/mASTM D4812落锤冲击 (23°C)102JASTM D3029拉伸冲击强度 5158kJ/m²ASTM D1822热性能额定值单位制测试方法载荷下热变形温度ASTM D648    0.45 MPa, 未退火, 6.40 mm146°CASTM D648    1.8 MPa, 未退火, 6.40 mm142°CASTM D648维卡软化温度154°CASTM D1525 6线形热膨胀系数 - 流动 (-40 到 95°C)3.2E-5cm/cm/°CASTM E831比热1210J/kg/°CASTM C351导热系数0.20W/m/KASTM C177RTI Elec120°CUL 746RTI Imp110°CUL 746RTI125°CUL 746电气性能额定值单位制测试方法体积电阻率> 1.0E+17ohms·cmASTM D257介电强度 (3.20 mm, in Air)18kV/mmASTM D149介电常数ASTM D150    50 Hz3.10ASTM D150    60 Hz3.10ASTM D150    1 MHz3.05ASTM D150耗散因数ASTM D150    50 Hz8.0E-4ASTM D150    60 Hz8.0E-4ASTM D150    1 MHz7.5E-3ASTM D150耐电弧性 7PLC 7ASTM D495相比耐漏电起痕指数(CTI)PLC 4UL 746高电弧燃烧指数(HAI)PLC 1UL 746高电压电弧起痕速率 (HVTR)PLC 3UL 746热丝引燃 (HWI)PLC 1UL 746可燃性额定值单位制测试方法UL 阻燃等级UL 94    1.52 mmV-0UL 94    3.00 mm5VAUL 94极限氧指数36%ASTM D2863注射额定值单位制干燥温度121°C干燥时间3.0 到 4.0hr干燥时间，最大48hr建议的最大水分含量0.020%建议注射量40 到 60%料筒后部温度288 到 310°C料筒中部温度299 到 321°C料筒前部温度310 到 332°C射嘴温度304 到 327°C加工（熔体）温度310 到 332°C模具温度82.0 到 116°C背压0.345 到 0.689MPa螺杆转速40 到 70rpm排气孔深度0.025 到 0.076mm