碳纤增强抗静电PC LEXAN LC108
PC 基础创新塑料(美国) LC108
LEXAN LC108 Resin SABIC Innovative Plastics Asia Pacific PC，
性能特点：碳纤8%，阻燃，抗静电，
物理性能：比重1.22，收缩率0.2-0.4%，吸水率0.13%，洛氏硬度88M，23℃悬臂冲击强度88J/M，热变形温度142℃，表面电阻率1.0E+8到1.0E+12ohm。
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc 1.22 g/cc ASTM D792
Water Absorption 0.13 %
@Time 86400 sec 0.13 %
@Time 24.0 hour ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
@Thickness 3.20 mm 0.0020 - 0.0040 in/in
@Thickness 0.126 in SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell M 88 88 ASTM D785
Tensile Strength, Yield 98.0 MPa 14200 psi SABIC - Japan Method
Elongation at Break 4.0 - 6.0 % 4.0 - 6.0 % SABIC - Japan Method
Flexural Strength 160 MPa 23200 psi ASTM D790
Flexural Modulus 5.98 GPa 867 ksi ASTM D790
Izod Impact, Notched 0.880 J/cm 1.65 ft-lb/in ASTM D256
Electrical Properties Metric English Comments
Surface Resistance 1.00e+8 - 1.00e+12 ohm 1.00e+8 - 1.00e+12 ohm ASTM D257
Thermal Properties Metric English Comments
CTE, linear 35.0 - 59.0 µm/m-°C
@Temperature -30.0 - 30.0 °C 19.4 - 32.8 µin/in-°F
@Temperature -22.0 - 86.0 °F TMA
Deflection Temperature at 0.46 MPa (66 psi) 142 °C
@Thickness 3.20 mm 288 °F
@Thickness 0.126 in unannealed; ASTM D648