物理性能额定值 (公制)额定值 (英制)测试方法密度1.43 g/cc0.0517 lb/in³Crystalline; ISO 1183Water Absorption at Saturation0.40 %@Temperature 23.0 °C0.40 %@Temperature 73.4 °FE; by immersion; ISO 62-10.45 %@Temperature 100 °C0.45 %@Temperature 212 °Fimmersion; ISO 62-1粘度475000 cP@Temperature 400 °C475000 cP@Temperature 752 °Fmelt; ISO 11443线性成型收缩率,Flow0.0030 cm/cm0.0030 in/in360°C nozzle, 160°C tool; ISO 294-4线性成型收缩率，横向0.0090 cm/cm0.0090 in/in380°C nozzle, 190°C tool; ISO 294-4Spiral Flow10.0 cm@Thickness 1.00 mm3.94 in@Thickness 0.0394 in380°C nozzle, 190°C tool机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)160 MPa@Temperature 23.0 °C23200 psi@Temperature 73.4 °FISO 527伸长率 (断裂)3.4 %@Temperature 23.0 °C3.4 %@Temperature 73.4 °FISO 527拉伸模量8.80 GPa@Temperature 23.0 °C1280 ksi@Temperature 73.4 °FISO 527弯曲强度250 MPa@Temperature 23.0 °C36300 psi@Temperature 73.4 °FISO 178弯曲模量8.30 GPa@Temperature 23.0 °C1200 ksi@Temperature 73.4 °FISO 178悬壁梁缺口冲击强度10.0 kJ/m²@Temperature 23.0 °C4.76 ft-lb/in²@Temperature 73.4 °FISO 180/A悬壁梁无缺口冲击强度65.0 kJ/m²@Temperature 23.0 °C30.9 ft-lb/in²@Temperature 73.4 °FISO 180/U电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093介电常数3.1@Frequency 1000 Hz, Temperature 23.0 °C3.1@Frequency 1000 Hz, Temperature 73.4 °FIEC 60250介电强度24.0 kV/mm@Thickness 2.00 mm610 kV/in@Thickness 0.0787 inIEC 60243-1耗散因数0.0050@Frequency 1.00e+6 Hz, Temperature 23.0 °C0.0050@Frequency 1.00e+6 Hz, Temperature 73.4 °FIEC 60250相比耐漏电起痕指数(CTI)150 V150 VIEC 60112热性能额定值 (公制)额定值 (英制)测试方法线性热膨胀系数45.0 µm/m-°C@Temperature =289 °FAverage above Tg; ISO 11359线形热膨胀系数 - 流动20.0 µm/m-°C@Temperature =289 °FAbove Tg; ISO 11359导热系数0.350 W/m-K2.43 BTU-in/hr-ft²-°FAlong flow; ISO 22007-40.300 W/m-K@Temperature 23.0 °C2.08 BTU-in/hr-ft²-°F@Temperature 73.4 °FAverage; ISO/CD 22007-4熔融温度343 °C649 °FISO 11357载荷下热变形温度(1.8 MPa)315 °C599 °FISO 75-f玻璃化转变温度，Tg143 °C289 °FOnset; ISO °C302 °FMidpoint; ISO 11357加工性能额定值 (公制)额定值 (英制)测试方法加工温度