能浮于水面的粉煤灰空心球，呈灰白色，壁薄中空，重量轻，容重为250－450kg/m3，粒径约0.1毫米，表面封闭而光滑，热导率小，耐火度≥1700℃，是优良的保温耐火材料，广泛用于轻质浇注料的生产和石油钻井方面。漂珠的化学成份以二氧化硅和三氧化二铝为主，具有颗粒细、中空、质轻、高强、耐磨、耐高温、保温绝缘、绝缘阻燃等多种功能，现已广泛应用于各个行业。
漂珠特性硬性结合耐火浇注料在常温下凝结硬化并通过水化作用而硬化，主要品种有硅酸盐水泥、普通铝酸钙水泥、
纯铝酸钙水泥、电熔纯铝酸钙水泥耐火浇注料等。化学结合浇注料在常温下一般通过加入促硬剂形成化学反应而硬化，主要品种有水玻璃、硫酸铝、磷酸盐耐火浇注料等。凝聚结合浇注料为在煅烧过程中经烧结作用而硬化，主要品种有粘土耐火浇注料等
Drift beads characteristics
1, high refractoriness, the main chemical compositions for silicon drift beads, aluminum oxide, silica (SiO2) about 50-65%, 3 oxidation 2 aluminium (Al2O3) about 25-35%.Because the melting point of silica (SiO2) is as high as 1725 degrees Celsius, 3 oxidation 2 aluminium (Al2O3), the melting point of 2050 degrees Celsius, are all high refractory material.Therefore, drift beads have high refractoriness, generally 1600-1600 degrees Celsius, make its excellent high performance refractories.
2, light, heat preservation and heat insulation: drift beads thin wall hollow, empty cavity for half a vacuum, only trace amounts of the gas (N2 and H2 and CO2, etc.), heat tran
1、高耐火度；漂珠的主要化学成分为硅、铝的氧化物，其中二氧化硅约为50－65％，三氧化二铝约为25－35％。因为二氧化硅的溶点高达摄氏1725度，三氧化二铝的溶点为摄氏2050度，均为高耐火物质。因此，漂珠具有极高的耐火度，一般达摄氏1600－1700度，使其成为优异的高性能耐火材料。
2、 质轻、保温隔热；漂珠壁薄中空，空腔内为半真空，只有极微量的气体（N2、H2及CO2等），热传导极慢极微。所以漂珠不但质轻（容重250－450公斤/m3），而且保温隔热优异（导热系数常温0.08－0.1），这为其在轻质保温隔热材料领域大显身手奠定了基础。
3、硬度大、强度高；由于漂珠是以硅铝氧化物矿物相（石英和莫来石）形成的坚硬玻璃体，硬度可达莫氏6－7级，静压强度高达70－140MPa，真密度2.10－2.20克/cm3，因此，漂珠具有很高的强度。
4、绝缘不导电；一般绝缘体的电阻均随温度的升高而降低，漂珠则相反，随温度的升高电阻增大。这一优点是其他绝缘材料都不具备的。所以，它可以制作是性能优异的绝缘材料。5、粒度细，比