增强级 PA6 德国巴斯夫 8333G 冲击改性 良好的成型性 电动工具 紧固件
发布时间：2025-06-20 17:07 点击:1次
增强级 PA6 德国巴斯夫 8333G 冲击改性 良好的成型性 电动工具 紧固件 Ultramid® 8333G Polyamide 6BASF Corporation33% 玻璃纤维增强材料产品说明：Ultramid 8333G HI is a 33% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. It is also available in heat stabilized (Ultramid 8333G HI HS) and/or pigmented versions.ApplicationsUltramid 8333G HI is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware.物性信息：基本信息黄卡编号E36632-231151填料/增强材料玻璃纤维增强材料, 33% 填料按重量添加剂冲击改性剂特性冲击改性刚性，良好良好的成型性能良好的强度用途车轮动力/其它工具紧固件外壳机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规外观可用颜色形式粒子加工方法注射成型物理性能干燥调节后的单位制测试方法比重1.34--g/cm³ASTM D792, ISO 1183收缩率 - 流动 (3.18 mm)0.30--%吸水率 24 hr0.90--%ASTM D570 23°C, 24 hr0.90--%ISO 62 饱和5.5--%ASTM D570 饱和, 23°C5.5--%ISO 62 平衡, 50% RH1.5--%ASTM D570 平衡, 23°C, 50% RH1.5--%ISO 62硬度干燥调节后的单位制测试方法洛氏硬度 (R 级)121--ASTM D785机械性能干燥调节后的单位制测试方法拉伸模量ISO 527-2 -40°C9200--MPaISO 527-2 23°C93004610MPaISO 527-2 121°C2660--MPaISO 527-2抗张强度 断裂, 23°C15290.0MPaASTM D638 断裂, 23°C14590.0MPaISO 527-2伸长率 (断裂, 23°C)3.56.0%ASTM D638, ISO 527-2弯曲模量 -40°C88209500MPaASTM D790 23°C80004830MPaASTM D790 65°C40403290MPaASTM D790 90°C32803250MPaASTM D790 121°C30402970MPaASTM D790 23°C72005030MPaISO 178 -40°C310297MPaASTM D790 23°C241124MPaASTM D790 65°C130110MPaASTM D790 90°C105100MPaASTM D790 121°C89.090.0MPaASTM D790 23°C215120MPaISO 178冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度ISO 179 -30°C10--kJ/m²ISO 179 23°C20--kJ/m²ISO 179简支梁无缺口冲击强度 (23°C)78--kJ/m²ISO 179悬壁梁缺口冲击强度 23°C240--J/mASTM D256 -40°C14--kJ/m²ISO 180 23°C21--kJ/m²ISO 180Drop Impact Resistance (23°C)4.88--J内部方法热性能干燥调节后的单位制测试方法热变形温度 0.45 MPa, 未退火220--°CISO 75-2/B 1.8 MPa, 未退火210--°CASTM D648 1.8 MPa, 未退火205--°CISO 75-2/A熔融峰值温度220--°CASTM D3418, ISO 3146线形热膨胀系数 流动2.4E-5--cm/cm/°C 横向8.4E-5--cm/cm/°CRTI ElecUL 746 0.800 mm105--°CUL 746 1.50 mm105--°CUL 746 3.00 mm105--°CUL 746RTI ImpUL 746增强级 PA6 德国巴斯夫 8333G 冲击改性 良好的成型性 电动工具 紧固件