抗紫外线 PA6 德国巴斯夫 8267GHS 抗蠕变 低翘曲 耐候 汽车外部零件 车轮应用 Ultramid® 8267G HS BK-106Polyamide 6BASF Corporation40% 玻璃矿物产品说明：Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The combination of mineral and glass fibers result in a high performance, low warp and cost effective engineering thermoplastic. It exhibits high strength, good UV resistance, rigidity and good heat distortion temperatures. It has a relatively high resistance to creep under load. The heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons.ApplicationsUltramid 8267G HS BK-106 is generally recommended for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds and all external parts exposed to the environment.物性信息：基本信息填料/增强材料玻璃\矿物, 40% 填料按重量添加剂热稳定剂特性低翘曲性刚性，高高强度抗紫外线性能良好良好的抗蠕变性耐化学性良好耐气候影响性能良好耐碳氢化合物耐油性能耐油脂性能热稳定性用途车轮汽车领域的应用汽车外部零件机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规外观黑色形式粒子加工方法注射成型物理性能额定值单位制测试方法比重1.48g/cm³ASTM D792, ISO 1183收缩率 - 流动 (3.18 mm)0.40%吸水率 24 hr0.90%ASTM D570 23°C, 24 hr0.90%ISO 62 饱和5.7%ASTM D570 饱和, 23°C5.7%ISO 62 平衡, 50% RH1.6%ASTM D570 平衡, 23°C, 50% RH1.6%ISO 62硬度额定值单位制测试方法洛氏硬度 (R 级)121ASTM D785机械性能额定值单位制测试方法拉伸模量ISO 527-2 -40°C10800MPaISO 527-2 23°C9200MPaISO 527-2 80°C3090MPaISO 527-2 121°C2620MPaISO 527-2抗张强度 断裂, -40°C178MPaASTM D638, ISO 527-2 断裂, 23°C125MPaASTM D638 断裂, 80°C59.0MPaASTM D638, ISO 527-2 断裂, 121°C51.0MPaASTM D638, ISO 527-2 断裂, 23°C115MPaISO 527-2伸长率 断裂, -40°C3.0%ASTM D638 断裂, 23°C2.0%ASTM D638, ISO 527-2 断裂, 80°C13%ASTM D638 断裂, 121°C11%ASTM D638弯曲模量 23°C7580MPaASTM D790 23°C200MPaASTM D790 23°C178MPaISO 178冲击性能额定值单位制测试方法简支梁缺口冲击强度 (23°C)5.5kJ/m²ISO 179简支梁无缺口冲击强度 (23°C)46kJ/m²ISO 179悬壁梁缺口冲击强度 23°C55J/mASTM D256 -40°C4.0kJ/m²ISO 180 23°C6.0kJ/m²ISO 180热性能额定值单位制测试方法热变形温度 0.45 MPa, 未退火215°CISO 75-2/B 1.8 MPa, 未退火202°CASTM D648 1.8 MPa, 未退火200°CISO 75-2/A熔融峰值温度220°CASTM D3418, ISO 3146线形热膨胀系数 - 流动3.1E-5cm/cm/°CASTM E831注射额定值单位制干燥温度83.0°C干燥时间2.0 到 4.0hr建议的最大水分含量0.15%加工（熔体）温度270 到 295°C模具温度80.0 到 95.0°C注塑压力3.50 到 12.5MPa注射速度快速抗紫外线 PA6 德国巴斯夫 8267GHS 抗蠕变 低翘曲 耐候 汽车外部零件 车轮应用