产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 阻燃性 | UL 94 | 0.8 | mm | |
| 阻燃性 | UL 94 | V-0 | |||
| 比重 | ASTM D-792 | 1.15 | |||
| 模具收缩率 | 3.2mm | ASTM D-792 | 1.1 | % | |
| 模具收缩率 | 1.6mm | ASTM D-792 | 0.8 | % | |
| 机械性能 | 断裂伸长率 | ASTM D-638 | 14 | % | |
| 拉伸强度 | ASTM D-638 | 89.6 | MPa | ||
| IZOD缺口冲击强度 | ASTM D-256 | 43 | J/m | ||
| 弯曲模量 | ASTM D-790 | 3450 | MPa | ||
| 热性能 | 热变形温度 | 1.80MPa | ASTM D-648 | 70 | ℃ |
| 熔点 | ASTM D-3418 | 264 | ℃ | ||
| 热变形温度 | 0.45MPa | ASTM D-648 | 230 | ℃ | |
| PA66 FR7025V0F 美国杜邦公司物性数据 |
| 规格级别: | 注塑级 | 外观颜色: | --- |
| 用途概述: | --- | ||
| 备注说明: | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 阻燃性 | --- | UL 94 | V-0 | --- |
| 阻燃性 | --- | UL 94 | 0.8 | mm | |
| 比重 | --- | ASTM D-792 | 1.15 | --- | |
| 模具收缩率 | 1.6mm | ASTM D-792 | 0.8 | % | |
| 模具收缩率 | 3.2mm | ASTM D-792 | 1.1 | % | |
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 89.6 | MPa |
| 断裂伸长率 | --- | ASTM D-638 | 14 | % | |
| 弯曲模量 | --- | ASTM D-790 | 3450 | MPa | |
| IZOD缺口冲击强度 | --- | ASTM D-256 | 43 | J/m | |
| 热 性 能 | 熔点 | --- | ASTM D-3418 | 264 | ℃ |
| 热变形温度 | 0.45MPa | ASTM D-648 | 230 | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | 70 | ||