热稳定 PA6 德国巴斯夫 8232G HSFR 高强度 阻燃 开关 线轴 连接器应用

热稳定 PA6 德国巴斯夫 8232G HSFR 高强度 阻燃 开关 线轴 连接器应用 Ultramid® 8232G HS FRPolyamide 6BASF Corporation25% 玻璃纤维增强材料产品说明：Ultramid 8232G HS FR is a 25% glass fiber reinforced, heat stabilized, flame retardant PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.ApplicationsUltramid 8232G HS FR is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.物性信息：基本信息黄卡编号E36632-231124填料/增强材料玻璃纤维增强材料, 25% 填料按重量添加剂热稳定剂特性刚性，高高强度较高的熔体稳定性热稳定性阻燃性用途家电部件开关连接器外壳线轴机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规形式粒子加工方法注射成型物理性能额定值单位制测试方法比重1.62g/cm³ASTM D792收缩率 - 流动 (3.18 mm)0.30%吸水率ASTM D570    24 hr0.90%ASTM D570    饱和4.0%ASTM D570    平衡, 50% RH1.1%ASTM D570硬度额定值单位制测试方法洛氏硬度 (R 级)121ASTM D785机械性能额定值单位制测试方法抗张强度 (断裂, 23°C)157MPaASTM D638伸长率 (断裂, 23°C)3.0%ASTM D638弯曲模量 (23°C)8970MPaASTM D790弯曲强度 (23°C)232MPaASTM D790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°C)110J/mASTM D256热性能额定值单位制测试方法载荷下热变形温度 (1.8 MPa, 未退火)195°CASTM D648熔融峰值温度220°CASTM D3418RTI ElecUL 746    0.840 mm130°CUL 746    1.50 mm130°CUL 746    2.50 mm130°CUL 746    3.00 mm130°CUL 746RTI ImpUL 746    0.840 mm105°CUL 746    1.50 mm115°CUL 746    2.50 mm115°CUL 746    3.00 mm115°CUL 746RTIUL 746    0.840 mm105°CUL 746    1.50 mm115°CUL 746    2.50 mm115°CUL 746    3.00 mm120°CUL 746电气性能额定值单位制测试方法体积电阻率 (1.50 mm)> 1.0E+13ohms·cmASTM D257介电强度 1(1.50 mm)29kV/mmASTM D149可燃性额定值单位制测试方法UL 阻燃等级UL 94    0.840 mmV-0UL 94    1.50 mmV-0UL 94    2.50 mmV-0 5VAUL 94    3.00 mmV-0 5VAUL 94注射额定值单位制干燥温度80.0°C干燥时间2.0 到 4.0hr建议的最大水分含量0.15%加工（熔体）温度250 到 290°C模具温度80.0 到 95.0°C注塑压力3.50 到 12.5MPa注射速度快速热稳定 PA6 德国巴斯夫 8232G HSFR 高强度 阻燃 开关 线轴 连接器应用 德国巴斯夫 PA6,8232G HSFR,热稳定 PA6,高强度pa6,阻燃级PA6德国巴斯夫 PA6,8232G HSFR,热稳定 PA6,高强度pa6,阻燃级PA6