防火PC 1301EP-30 韩国LG 低粘度 耐热 耐冲击

产品说明：Description: LUPOY PC 1301EP-30 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics: Very low viscosity and Good mold releaseApplications: DVD security boxes, Mobile phone keypads, DVD security boxes and Thin componentsCAS: 103598-77-2Information provided by LG Chemical物性信息：物理性能额定值 (公制)额定值 (英制)测试方法比重1.20 g/cc1.20 g/ccASTM D792吸水率0.32 %@Temperature 23.0 °C0.32 %@Temperature 73.4 °Fequilibrium, 50% RH; ASTM D5700.15 %@Temperature 23.0 °C, Time 86400 sec0.15 %@Temperature 73.4 °F, Time 24.0 hourASTM D570线性成型收缩率,Flow0.00050 - 0.00070 cm/cm0.00050 - 0.00070 in/inASTM D955熔体流动速率30 g/10 min@Load 1.20 kg, Temperature 300 °C30 g/10 min@Load 2.65 lb, Temperature 572 °FASTM D1238机械性能额定值 (公制)额定值 (英制)测试方法极限抗拉强度61.0 MPa8850 psiASTM D638抗张强度(屈服)60.0 MPa8700 psi50mm/min; ASTM D638伸长率 (断裂)150 %150 %ASTM D638屈服伸长率6.0 %6.0 %ASTM D638拉伸模量2.34 GPa340 ksiASTM D638弯曲强度96.0 MPa13900 psiASTM D790弯曲模量2.41 GPa350 ksiASTM D790悬壁梁缺口冲击强度6.939 J/cm@Thickness 3.20 mm, Temperature 23.0 °C13.00 ft-lb/in@Thickness 0.126 in, Temperature 73.4 °F0.25 mm notch; ASTM D256悬壁梁无缺口冲击强度NB@Temperature 23.0 °CNB@Temperature 73.4 °FASTM D256电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率2.00e+17 ohm-cm2.00e+17 ohm-cmASTM D257介电常数3.0@Frequency 60.0 Hz3.0@Frequency 60.0 HzASTM D150介电强度17.0 kV/mm432 kV/inASTM D149耗散因数0.0010@Frequency 60.0 Hz0.0010@Frequency 60.0 HzASTM D150耐电弧性120 - 180 sec120 - 180 secASTM D495相比耐漏电起痕指数(CTI)250 V@Thickness 2.00 mm250 V@Thickness 0.0787 inIEC 112热丝引燃 (HWI)30 - 60 sec@Thickness >=1.50 mm30 - 60 sec@Thickness >=0.0591 in60 - 120 sec@Thickness >=3.00 mm60 - 120 sec@Thickness >=0.118 in高电弧燃烧指数(HAI)60 - 120 arcs@Thickness 1.50 mm60 - 120 arcs@Thickness 0.0591 in60 - 120 arcs@Thickness 3.00 mm60 - 120 arcs@Thickness 0.118 in高压电弧跟踪率，HVTR25.4 - 50.0 mm/min1.00 - 1.97 in/min热性能额定值 (公制)额定值 (英制)测试方法线性热膨胀系数68.0 ?m/m-°C@Temperature -40.0 - 82.0 °C37.8 ?in/in-°F@Temperature -40.0 - 180 °FASTM D696Hot Ball Pressure Test>= 125 °C>= 257 °FIEC 598-1载荷下热变形温度(0.46 MPa)139 °C@Thickness 4.00 mm282 °F@Thickness 0.157 inAnnealed; ASTM D648Deflection Temperature at 1.8 MPa (264 psi)122 °C@Thickness 4.00 mm252 °F@Thickness 0.157 inUnannealed; ASTM D648136 °C@Thickness 4.00 mm277 °F@Thickness 0.157 inAnnealed; ASTM D648维卡软化温度144 °C@Load 5.10 kg291 °F@Load 11.2 lb50°C/hr; ASTM D1525软化温度150 - 200 °C302 - 392 °Fmelting point per MSDSUL RTI125 °C@Thickness >=1.50 mm257 °F@Thickness >=0.0591 in125 °C@Thickness >=3.00 mm257 °F@Thickness >=0.118 inUL RTI，机械冲击115 °C@Thickness >=1.50 mm239 °F@Thickness >=0.0591 in115 °C@Thickness >=3.00 mm239 °F@Thickness >=0.118 inUL RTI，机械无冲击125 °C@Thickness >=1.50 mm257 °F@Thickness >=0.0591 in125 °C@Thickness >=3.00 mm257 °F@Thickness >=0.118 in可燃性(UL94)V-2@Thickness 0.500 mmV-2@Thickness 0.0197 inASTM D635V-2@Thickness 1.60 mmV-2@Thickness 0.0630 inASTM D635V-2@Thickness 2.50 mmV-2@Thickness 0.0984 inASTM D635V-2@Thickness 3.00 mmV-2@Thickness 0.118 inASTM D635Flash Point>= 450 °C>= 842 °F极限氧指数26 %26 %ASTM D2863灼热丝试验850 °C@Thickness 2.00 mm, Time 5.00 sec1560 °F@Thickness 0.0787 in, Time 0.00139 hourIEC 695-2-1光学性能额定值 (公制)额定值 (英制)测试方法折射率1.5861.586ASTM D542雾度0.70 - 1.5 %0.70 - 1.5 %ASTM D1003Transmission, Visible89 %89 %ASTM D1003材料描述测试方法Autoignition Temperature>450°CAverage Extent of BurningASTM D635